10H13G12BS2N2D2 (10H13P2BS2N2D2, DI59)
For the production of seamless cold, teplodeformirovannyh, hot-including hot-pressed and hot-reduced pipes for steam boilers and piping systems with high and supercritical steam parameters
Classification
| Country | Section | Category |
|---|---|---|
| CIS, Russia, Ukraine | Heat resistant steels and alloys | Heat resistant high alloy steel |
Chemical composition
| Standard | Fe, % | Si, % | B, % | Mn, % | Cr, % | Cu, % | Ni, % | Zr, % | Al, % | Ce, % | P, % | C, % | S, % | Nb, % | Tl, % |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| TU 14-3Р-55 - 2001 | 64.617–70.24 | 1.8–2.2 | < 0.003 | 12–13.5 | 11.5–13 | 2–2.5 | 1.8–2.5 | < 0.1 | < 0.25 | < 0.08 | < 0.03 | 0.06–0.1 | < 0.02 | 0.6–1 | < 0.1 |
Information on suppliers
Mechanical properties at 20 °C
| Rolling | Standard | Size, mm | Tension | Classifiers | $$\sigma _{U}$$, $$MPa$$ | $$\sigma_{Y}$$, $$MPa$$ | $$\psi$$, % | d5, % | Treatment |
|---|---|---|---|---|---|---|---|---|---|
| Trumpet | TU 14-3Р-55 - 2001 | Longitudinal | 588 | 216 | 50 | 40 |
Standards
| Standard | Description |
|---|---|
| TU 14-3Р-55 - 2001 |
Description of chemical elements
| Element | Units of measurement | Description |
|---|---|---|
| Fe | % | Iron |
| Si | % | Silicon |
| B | % | Bor |
| Mn | % | Manganese |
| Cr | % | Chrome |
| Cu | % | Copper |
| Ni | % | Nickel |
| Zr | % | Zirconium |
| Al | % | Aluminium |
| Ce | % | Cerium |
| P | % | Phosphorus |
| C | % | Carbon |
| S | % | Sulfur |
| Nb | % | Niobium |
| Tl | % | Thallium |
Description of mechanical properties
| Parameter | Units of measurement | Description |
|---|---|---|
| d5 | % | Elongation at break |
| $$\sigma_{Y}$$ | $$MPa$$ | Yield strength |
| $$\sigma _{U}$$ | $$MPa$$ | Ultimate tensile strength |
| $$\psi$$ | % | Reduction in cross section on fracture |