1201

For the manufacture of welded products operating operating at temperatures down to -253 deg.

Classification

Country Section Category
CIS, Russia, Ukraine Aluminum, aluminum alloys Wrought Aluminum Alloys

Chemical composition

Standard Fe, % Si, % Mg, % Mn, % Ti, % Cu, % Zn, % V, % Zr, % Al, %
GOST 4784-97 < 0.3 < 0.2 < 0.02 0.2–0.4 0.02–0.1 5.8–6.8 < 0.1 0.05–0.15 0.1–0.25 91.68–93.83

Information on suppliers

Physical characteristics

Temperature, °C $$\rho$$, $$\frac{kg}{m^3}$$
20 2850

Mechanical properties at 20 °C

Rolling Standard Size, mm Tension Classifiers $$\sigma _{U}$$, $$MPa$$ $$\sigma_{P}$$, $$MPa$$ $$\epsilon_L$$, % Treatment
Sheet 440 350 8

Technological Properties

Weldability
no limits

Analogues

USA
AA2219

Standards

Standard Description
GOST 4784-97

Description of chemical elements

Element Units of measurement Description
Fe % Iron
Si % Silicon
Mg % Magnesium
Mn % Manganese
Ti % Titan
Cu % Copper
Zn % Zinc
V % Vanadium
Zr % Zirconium
Al % Aluminium

Description of physical characteristics

Parameter Units of measurement Description
$$\rho$$ $$\frac{kg}{m^3}$$ The density of the material

Description of mechanical properties

Parameter Units of measurement Description
$$\sigma _{U}$$ $$MPa$$ Ultimate tensile strength
$$\sigma_{P}$$ $$MPa$$ Proportionality limit
$$\epsilon_L$$ % Elongation at break (longitudinal)

Designation of types of weldability

Parameter Units of measurement Description
no limits Welding is performed without heating and without subsequent heat treatment
Boundedly welded Welding is possible with heating up to 100–120 °C and subsequent heat treatment
Difficult to weld For obtaining quality welded joints, additional operations are required: heating up to 200–300 °C for welding, heat treatment after welding — annealing
Not applicable for welded structures