14H18N4G4L (10H18N4G4L)

Different Items (collectors of exhaust systems, furnace parts and fittings, etc.), operating at temperatures up to 400 ° C; austenitic steel — martensitic class

Classification

Country	Section	Category
Country	Section	Category
CIS, Russia, Ukraine	Steels and alloys for castings	Steel for casting with special properties

Chemical composition

Standard	Fe, %	Si, %	Mn, %	Cr, %	Ni, %	P, %	C, %	S, %
Standard	Fe, %	Si, %	Mn, %	Cr, %	Ni, %	P, %	C, %	S, %
GOST 977-88	68.795–75.8	0.2–1	4–5	16–20	4–5	< 0.035	< 0.14	< 0.03

Information on suppliers

Wish to advertise here?

Mechanical properties at 20 °C

Rolling	Standard	Size, mm	Tension	Classifiers	$\sigma _{U}$ , $MPa$	$\sigma_{P}$ , $MPa$	$\epsilon_L$ , %	$\psi$ , %	$KCU\cdot 10^{3}$ , $\frac{J}{m^2}$	Treatment
Rolling	Standard	Size, mm	Tension	Classifiers	$\sigma _{U}$ , $MPa$	$\sigma_{P}$ , $MPa$	$\epsilon_L$ , %	$\psi$ , %	$KCU\cdot 10^{3}$ , $\frac{J}{m^2}$	Treatment
Castings	GOST 977-88				441	245	25	35	981	Hardening of 1020-1070 ° C, cooling water

Heat Treatment Modes

Treatment
Treatment
Hardening 1020 - 1070 ° C, cooling in water

Standards

Standard	Description
Standard	Description
GOST 977-88

Description of chemical elements

Element	Units of measurement	Description
Element	Units of measurement	Description
Fe	%	Iron
Si	%	Silicon
Mn	%	Manganese
Cr	%	Chrome
Ni	%	Nickel
P	%	Phosphorus
C	%	Carbon
S	%	Sulfur

Description of mechanical properties

Parameter	Units of measurement	Description
Parameter	Units of measurement	Description
$\sigma _{U}$	$MPa$	Ultimate tensile strength
$\sigma_{P}$	$MPa$	Proportionality limit
$\epsilon_L$	%	Elongation at break (longitudinal)
$\psi$	%	Reduction in cross section on fracture
$KCU\cdot 10^{3}$	$\frac{J}{m^2}$	Impact toughness