14HGS

Alloy steel hromokremmartsantsovaya. According to GOST 5520−79 from 01/01/1, steel is not allowed to be used in the newly created and modernized equipment.

Electro Pipe main gas pipelines of high pressure; weldments, sheet, valve design details.

Classification

Country Section Category
CIS, Russia, Ukraine Structural steel Low alloy structural steel for welded structures

Chemical composition

Standard Fe, % Si, % Mn, % Cr, % Cu, % Ni, % As, % P, % C, % S, % N, %
GOST 19281-89 96.273–98.09 0.4–0.7 0.9–1.3 0.5–0.8 < 0.3 < 0.3 < 0.08 < 0.035 0.11–0.16 < 0.04 < 0.012

Information on suppliers

Mechanical properties at 20 °C

Rolling Standard Size, mm Tension Classifiers $$\sigma _{U}$$, $$MPa$$ $$\sigma_{P}$$, $$MPa$$ $$\epsilon_L$$, % $$KCU\cdot 10^{3}$$, $$\frac{J}{m^2}$$ Treatment
Sheet GOST 5520-79 490 345 22 340–390

Technological Properties

Weldability Flake Susceptibility Propensity to temper brittleness
Boundedly welded not sensitive inclined

Standards

Standard Description
GOST 19281-89

Description of chemical elements

Element Units of measurement Description
Fe % Iron
Si % Silicon
Mn % Manganese
Cr % Chrome
Cu % Copper
Ni % Nickel
As % Arsenic
P % Phosphorus
C % Carbon
S % Sulfur
N % Nitrogen

Description of mechanical properties

Parameter Units of measurement Description
$$\sigma _{U}$$ $$MPa$$ Ultimate tensile strength
$$\sigma_{P}$$ $$MPa$$ Proportionality limit
$$\epsilon_L$$ % Elongation at break (longitudinal)
$$KCU\cdot 10^{3}$$ $$\frac{J}{m^2}$$ Impact toughness

Designation of types of weldability

Parameter Units of measurement Description
no limits Welding is performed without heating and without subsequent heat treatment
Boundedly welded Welding is possible with heating up to 100–120 °C and subsequent heat treatment
Difficult to weld For obtaining quality welded joints, additional operations are required: heating up to 200–300 °C for welding, heat treatment after welding — annealing
Not applicable for welded structures