15G2SF

Unalloyed high-quality manganese-vanadium steel.

For welded structures

Classification

Country	Section	Category
Country	Section	Category
CIS, Russia, Ukraine	Structural steel	Low alloy structural steel for welded structures

Chemical composition

Standard	Fe, %	Si, %	Mn, %	Cr, %	Cu, %	Ni, %	V, %	As, %	P, %	C, %	S, %	N, %
Standard	Fe, %	Si, %	Mn, %	Cr, %	Cu, %	Ni, %	V, %	As, %	P, %	C, %	S, %	N, %
GOST 19281-89	96.253–98.13	0.4–0.7	1.3–1.7	< 0.3	< 0.3	< 0.3	0.05–0.1	< 0.08	< 0.035	0.12–0.18	< 0.04	< 0.012

Information on suppliers

Wish to advertise here?

Mechanical properties at 20 °C

Rolling	Standard	Size, mm	Tension	Classifiers	$\sigma _{U}$ , $MPa$	$\sigma_{Y}$ , $MPa$	$\epsilon_L$ , %	Treatment
Rolling	Standard	Size, mm	Tension	Classifiers	$\sigma _{U}$ , $MPa$	$\sigma_{Y}$ , $MPa$	$\epsilon_L$ , %	Treatment
Sheet	GOST 19282-73	10–20			560	400	18
Sheet	GOST 19281-2014	< 50			510	390	19
Grade	GOST 19281-2014	< 50			510	390	18

Technological Properties

Weldability
Weldability
no limits

Standards

Standard	Description
Standard	Description
GOST 19281-89

Description of chemical elements

Element	Units of measurement	Description
Element	Units of measurement	Description
Fe	%	Iron
Si	%	Silicon
Mn	%	Manganese
Cr	%	Chrome
Cu	%	Copper
Ni	%	Nickel
V	%	Vanadium
As	%	Arsenic
P	%	Phosphorus
C	%	Carbon
S	%	Sulfur
N	%	Nitrogen

Description of mechanical properties

Parameter	Units of measurement	Description
Parameter	Units of measurement	Description
$\sigma_{Y}$	$MPa$	Yield strength
$\sigma _{U}$	$MPa$	Ultimate tensile strength
$\epsilon_L$	%	Elongation at break (longitudinal)

Designation of types of weldability

Parameter	Units of measurement	Description
Parameter	Units of measurement	Description
no limits		Welding is performed without heating and without subsequent heat treatment
Boundedly welded		Welding is possible with heating up to 100–120 °C and subsequent heat treatment
Difficult to weld		For obtaining quality welded joints, additional operations are required: heating up to 200–300 °C for welding, heat treatment after welding — annealing
Not applicable for welded structures