15GS (15GS-Sh)
Steel is not inclined. to temper embrittlement. Another designation 15GS-Sh. Weldability without restrictions. Flock sensitivity: not sensitive.
stationary pipelines feedwater TDS boilers operating at a temperature of 280 degrees C
Classification
| Country |
Section |
Category |
| CIS, Russia, Ukraine |
Structural steel |
Low alloy structural steel for welded structures |
Chemical composition
| Standard |
Fe, % |
Si, % |
Mn, % |
Cr, % |
Cu, % |
Ni, % |
P, % |
C, % |
S, % |
|---|
| TU 1310-030-00212179-2007 |
96.55–98.28 |
0.7–1 |
0.9–1.3 |
< 0.3 |
< 0.3 |
< 0.3 |
< 0.035 |
0.12–0.18 |
< 0.03 |
Information on suppliers
Mechanical properties at 20 °C
| Rolling |
Standard |
Size, mm |
Tension |
Classifiers |
$$\sigma _{U}$$, $$MPa$$ |
$$\epsilon_L$$, % |
$$\psi$$, % |
Treatment |
|---|
| Trumpet |
|
|
|
|
500 |
18 |
45 |
Normalization of 900-930 ° C, air |
| Trumpet |
|
|
|
|
500 |
16 |
40 |
Normalization of 900-930 ° C, air |
Technological Properties
| Weldability |
Flake Susceptibility |
Propensity to temper brittleness |
|---|
| no limits |
not sensitive |
not inclined |
Standards
Description of chemical elements
| Element |
Units of measurement |
Description |
| Fe |
% |
Iron |
| Si |
% |
Silicon |
| Mn |
% |
Manganese |
| Cr |
% |
Chrome |
| Cu |
% |
Copper |
| Ni |
% |
Nickel |
| P |
% |
Phosphorus |
| C |
% |
Carbon |
| S |
% |
Sulfur |
Description of mechanical properties
| Parameter |
Units of measurement |
Description |
| $$\sigma _{U}$$ |
$$MPa$$ |
Ultimate tensile strength |
| $$\epsilon_L$$ |
% |
Elongation at break (longitudinal) |
| $$\psi$$ |
% |
Reduction in cross section on fracture |
Designation of types of weldability
| Parameter |
Units of measurement |
Description |
| no limits |
|
Welding is performed without heating and without subsequent heat treatment |
| Boundedly welded |
|
Welding is possible with heating up to 100–120 °C and subsequent heat treatment |
| Difficult to weld |
|
For obtaining quality welded joints, additional operations are required: heating up to 200–300 °C for welding, heat treatment after welding — annealing |
| Not applicable for welded structures |
|
|