20G1FL (20GFL)
frame, beams, housing and others. wagons details
Classification
| Country | Section | Category |
|---|---|---|
| CIS, Russia, Ukraine | Steels and alloys for castings | Ordinary steel for castings |
Chemical composition
| Standard | Fe, % | Si, % | Mn, % | Ti, % | V, % | P, % | C, % | S, % |
|---|---|---|---|---|---|---|---|---|
| GOST 977-88 | 97.58–98.68 | 0.2–0.5 | 0.9–1.4 | < 0.05 | 0.06–0.12 | < 0.05 | 0.16–0.25 | < 0.05 |
Information on suppliers
Mechanical properties at 20 °C
| Rolling | Standard | Size, mm | Tension | Classifiers | $$\sigma _{U}$$, $$MPa$$ | $$\sigma_{P}$$, $$MPa$$ | $$\epsilon_L$$, % | $$\psi$$, % | $$KCU\cdot 10^{3}$$, $$\frac{J}{m^2}$$ | Treatment |
|---|---|---|---|---|---|---|---|---|---|---|
| Castings | GOST 977-88 | 510 | 314 | 17 | 25 | 491 | Tempering 930-970 ° C, 600-650 ° C and Holidays |
Heat Treatment Modes
| Treatment |
|---|
| Normalization 930 - 970 ° C, Release 600 - 650 ° C |
Analogues
| USA |
|---|
| J13002 |
Standards
| Standard | Description |
|---|---|
| GOST 977-88 |
Description of chemical elements
| Element | Units of measurement | Description |
|---|---|---|
| Fe | % | Iron |
| Si | % | Silicon |
| Mn | % | Manganese |
| Ti | % | Titan |
| V | % | Vanadium |
| P | % | Phosphorus |
| C | % | Carbon |
| S | % | Sulfur |
Description of mechanical properties
| Parameter | Units of measurement | Description |
|---|---|---|
| $$\sigma _{U}$$ | $$MPa$$ | Ultimate tensile strength |
| $$\sigma_{P}$$ | $$MPa$$ | Proportionality limit |
| $$\epsilon_L$$ | % | Elongation at break (longitudinal) |
| $$\psi$$ | % | Reduction in cross section on fracture |
| $$KCU\cdot 10^{3}$$ | $$\frac{J}{m^2}$$ | Impact toughness |