20H12N2V2MF

compressor disks, blades and other loaded parts, long operating at temperatures up to 600 degrees.

Classification

Country	Section	Category
Country	Section	Category
CIS, Russia, Ukraine	Heat resistant steels and alloys	Heat resistant high alloy steel

Chemical composition

Standard	Fe, %	Si, %	Mn, %	Cr, %	Ni, %	V, %	P, %	C, %	S, %	Mo, %	W, %
Standard	Fe, %	Si, %	Mn, %	Cr, %	Ni, %	V, %	P, %	C, %	S, %	Mo, %	W, %
	82.015–85.78	< 0.6	< 0.6	10.5–12	1.5–1.8	0.18–0.3	< 0.03	0.09–0.13	< 0.025	0.35–0.5	1.6–2

Information on suppliers

Wish to advertise here?

Physical characteristics

Temperature, °C	$E\cdot 10^{9}$ , $MPa$	$\alpha\cdot 10^{6}$ , $K^{-1}$	$\varkappa$ , $\frac{W}{m\cdot K}$	$\rho$ , $\frac{kg}{m^3}$
Temperature, °C	$E\cdot 10^{9}$ , $MPa$	$\alpha\cdot 10^{6}$ , $K^{-1}$	$\varkappa$ , $\frac{W}{m\cdot K}$	$\rho$ , $\frac{kg}{m^3}$
20	200		20.9	7800
100	195	11	22.3
200	185	11.7	24
300	175	12.2	25.5
400	165	13.3	27.2
500	145	13	28
600	109	13	28.5

Mechanical properties at 20 °C

Rolling	Standard	Size, mm	Tension	Classifiers	$\sigma _{U}$ , $MPa$	$\sigma_{P}$ , $MPa$	$\epsilon_L$ , %	Treatment
Rolling	Standard	Size, mm	Tension	Classifiers	$\sigma _{U}$ , $MPa$	$\sigma_{P}$ , $MPa$	$\epsilon_L$ , %	Treatment
Sheet		0.8–4			650	450	19	Accommodation 730-750 ° C, 2 hours, air cooling

Technological Properties

Weldability
Weldability
no limits

Description of chemical elements

Element	Units of measurement	Description
Element	Units of measurement	Description
Fe	%	Iron
Si	%	Silicon
Mn	%	Manganese
Cr	%	Chrome
Ni	%	Nickel
V	%	Vanadium
P	%	Phosphorus
C	%	Carbon
S	%	Sulfur
Mo	%	Molybdenum
W	%	Tungsten

Description of physical characteristics

Parameter	Units of measurement	Description
Parameter	Units of measurement	Description
$E\cdot 10^{9}$	$MPa$	Elastic modulus
$\alpha\cdot 10^{6}$	$K^{-1}$	Coefficient of thermal (linear) expansion (range 20°C–T)
$\varkappa$	$\frac{W}{m\cdot K}$	Coefficient of thermal conductivity (the heat capacity of the material)
$\rho$	$\frac{kg}{m^3}$	The density of the material

Description of mechanical properties

Parameter	Units of measurement	Description
Parameter	Units of measurement	Description
$\sigma _{U}$	$MPa$	Ultimate tensile strength
$\sigma_{P}$	$MPa$	Proportionality limit
$\epsilon_L$	%	Elongation at break (longitudinal)

Designation of types of weldability

Parameter	Units of measurement	Description
Parameter	Units of measurement	Description
no limits		Welding is performed without heating and without subsequent heat treatment
Boundedly welded		Welding is possible with heating up to 100–120 °C and subsequent heat treatment
Difficult to weld		For obtaining quality welded joints, additional operations are required: heating up to 200–300 °C for welding, heat treatment after welding — annealing
Not applicable for welded structures