23HGS2MFL

Responsible destination details to the wall thickness of 30 mm, running in a cyclic and impact and shock under abrasive wear

Classification

Country	Section	Category
Country	Section	Category
CIS, Russia, Ukraine	Steels and alloys for castings	Ordinary steel for castings

Chemical composition

Standard	Fe, %	Si, %	Mn, %	Cr, %	V, %	P, %	C, %	S, %	Mo, %
Standard	Fe, %	Si, %	Mn, %	Cr, %	V, %	P, %	C, %	S, %	Mo, %
GOST 977-88	95.56–96.57	1.8–2	0.5–0.8	0.6–0.9	0.1–0.15	< 0.025	0.18–0.24	< 0.025	0.25–0.3

Information on suppliers

Wish to advertise here?

Mechanical properties at 20 °C

Rolling	Standard	Size, mm	Tension	Classifiers	$\sigma _{U}$ , $MPa$	$\sigma_{P}$ , $MPa$	$\epsilon_L$ , %	$\psi$ , %	$KCU\cdot 10^{3}$ , $\frac{J}{m^2}$	Treatment
Rolling	Standard	Size, mm	Tension	Classifiers	$\sigma _{U}$ , $MPa$	$\sigma_{P}$ , $MPa$	$\epsilon_L$ , %	$\psi$ , %	$KCU\cdot 10^{3}$ , $\frac{J}{m^2}$	Treatment
Castings	GOST 977-88				1275	1079	6	24	392	Hardening of 980-1000 ° C, 200-230 ° C and Holidays

Heat Treatment Modes

Treatment
Treatment
Pretreatment - Normalization 1000 - 1040 ° C, Release 720 - 740 ° C
Final processing - Hardening 1000 - 1020 ° C, Release 180 - 220 ° C

Standards

Standard	Description
Standard	Description
GOST 977-88

Description of chemical elements

Element	Units of measurement	Description
Element	Units of measurement	Description
Fe	%	Iron
Si	%	Silicon
Mn	%	Manganese
Cr	%	Chrome
V	%	Vanadium
P	%	Phosphorus
C	%	Carbon
S	%	Sulfur
Mo	%	Molybdenum

Description of mechanical properties

Parameter	Units of measurement	Description
Parameter	Units of measurement	Description
$\sigma _{U}$	$MPa$	Ultimate tensile strength
$\sigma_{P}$	$MPa$	Proportionality limit
$\epsilon_L$	%	Elongation at break (longitudinal)
$\psi$	%	Reduction in cross section on fracture
$KCU\cdot 10^{3}$	$\frac{J}{m^2}$	Impact toughness