27HN2MFL
for the manufacture of tooth-cast elements and their fasteners (staples, wedges) shovels.
Classification
| Country | Section | Category |
|---|---|---|
| CIS, Russia, Ukraine | Steels and alloys for castings | Steel for casting with special properties |
Chemical composition
| Standard | Fe, % | Si, % | Mn, % | Cr, % | Cu, % | Ni, % | V, % | P, % | C, % | S, % | Mo, % |
|---|---|---|---|---|---|---|---|---|---|---|---|
| GOST 21357-87 | 94.19–96.14 | 0.2–0.42 | 0.6–0.9 | 0.8–1.2 | < 0.3 | 1.65–2 | 0.08–0.15 | < 0.02 | 0.23–0.3 | < 0.02 | 0.3–0.5 |
Information on suppliers
Mechanical properties at 20 °C
| Rolling | Standard | Size, mm | Tension | Classifiers | $$\sigma _{U}$$, $$MPa$$ | $$\sigma_{Y}$$, $$MPa$$ | $$\psi$$, % | d5, % | Treatment |
|---|---|---|---|---|---|---|---|---|---|
| Castings | GOST 21357-87 | 1000 | 800 | 22 | 10 | Water hardening 880 - 920 ° C, Release 570 - 590 ° C |
Heat Treatment Modes
| Treatment |
|---|
| Water hardening 880 - 920 ° C, Release 570 - 590 ° C |
Standards
| Standard | Description |
|---|---|
| GOST 21357-87 |
Description of chemical elements
| Element | Units of measurement | Description |
|---|---|---|
| Fe | % | Iron |
| Si | % | Silicon |
| Mn | % | Manganese |
| Cr | % | Chrome |
| Cu | % | Copper |
| Ni | % | Nickel |
| V | % | Vanadium |
| P | % | Phosphorus |
| C | % | Carbon |
| S | % | Sulfur |
| Mo | % | Molybdenum |
Description of mechanical properties
| Parameter | Units of measurement | Description |
|---|---|---|
| d5 | % | Elongation at break |
| $$\sigma_{Y}$$ | $$MPa$$ | Yield strength |
| $$\sigma _{U}$$ | $$MPa$$ | Ultimate tensile strength |
| $$\psi$$ | % | Reduction in cross section on fracture |