30HGSN2A (30HGSNA)

Gears, flanges, fists, fingers, rollers, shafts, pins, and other senior heavy duty parts.

Classification

Country Section Category
CIS, Russia, Ukraine Structural steel Alloyed structural steel

Chemical composition

Standard Fe, % Si, % Mn, % Cr, % Cu, % Ni, % P, % C, % S, %
GOST 4543-71 93.81–95.53 0.9–1.2 1–1.3 0.9–1.2 < 0.3 1.4–1.8 < 0.025 0.27–0.34 < 0.025

Information on suppliers

Physical characteristics

Temperature, °C $$E\cdot 10^{9}$$, $$MPa$$ $$\alpha\cdot 10^{6}$$, $$K^{-1}$$ $$\varkappa$$, $$\frac{W}{m\cdot K}$$ $$\rho$$, $$\frac{kg}{m^3}$$ $$c\cdot 10^{-3}$$, $$\frac{J}{kg\cdot K}$$ $$R\cdot 10^{-6}$$, $$\Omega\cdot m$$
20 195 28.5 7770 0.44
100 10.6 29.4 0.503
200 11.2 30.6 0.545
300 180 13 31.4 0.587
400 168 14.9
500 135

Mechanical properties at 20 °C

Rolling Standard Size, mm Tension Classifiers $$\sigma _{U}$$, $$MPa$$ $$\sigma_{P}$$, $$MPa$$ $$\epsilon_L$$, % $$\psi$$, % $$KCU\cdot 10^{3}$$, $$\frac{J}{m^2}$$ Treatment
Trumpet GOST 21729 - 76 588 15
Rod GOST 4543-71 1620 1375 9 45 590 Hardening and tempering
The plates GOST 11269-76 490–830 19 Normalization
The plates GOST 11269-76 1570 9 590 Hardening and tempering
Sheet GOST 11268 - 76 590–830 19 Normalization
Sheet GOST 11268 - 76 1570 9 Hardening and tempering

Brinell hardness number

Rolling Standard Classifiers Value, HBW
Alloy GOST 4543-71 annealing 255
The plates GOST 11269-76 normalization 163–229

Technological Properties

Weldability Flake Susceptibility Propensity to temper brittleness
Difficult to weld sensitive inclined

Critical point temperatures

Ac1, K Ac3(Acm), K Mn, K
705 800 321

Standards

Standard Description
GOST 4543-71

Description of chemical elements

Element Units of measurement Description
Fe % Iron
Si % Silicon
Mn % Manganese
Cr % Chrome
Cu % Copper
Ni % Nickel
P % Phosphorus
C % Carbon
S % Sulfur

Description of physical characteristics

Parameter Units of measurement Description
$$E\cdot 10^{9}$$ $$MPa$$ Elastic modulus
$$\alpha\cdot 10^{6}$$ $$K^{-1}$$ Coefficient of thermal (linear) expansion (range 20°C–T)
$$\varkappa$$ $$\frac{W}{m\cdot K}$$ Coefficient of thermal conductivity (the heat capacity of the material)
$$\rho$$ $$\frac{kg}{m^3}$$ The density of the material
$$c\cdot 10^{-3}$$ $$\frac{J}{kg\cdot K}$$ The specific heat of the material (range 20°C–T)
$$R\cdot 10^{-6}$$ $$\Omega\cdot m$$ Electrical resistivity

Description of mechanical properties

Parameter Units of measurement Description
$$\sigma _{U}$$ $$MPa$$ Ultimate tensile strength
$$\sigma_{P}$$ $$MPa$$ Proportionality limit
$$\epsilon_L$$ % Elongation at break (longitudinal)
$$\psi$$ % Reduction in cross section on fracture
$$KCU\cdot 10^{3}$$ $$\frac{J}{m^2}$$ Impact toughness

Designation of types of weldability

Parameter Units of measurement Description
no limits Welding is performed without heating and without subsequent heat treatment
Boundedly welded Welding is possible with heating up to 100–120 °C and subsequent heat treatment
Difficult to weld For obtaining quality welded joints, additional operations are required: heating up to 200–300 °C for welding, heat treatment after welding — annealing
Not applicable for welded structures

Description of temperatures of critical points

Parameter Units of measurement Description
Ac1 K
Ac3(Acm) K
Mn K