30HS2
Weldability without restrictions.
manufacturing valves periodic profile of At1200 (Al-VII), designed for reinforcement of ordinary and prestressed concrete structures
Classification
| Country |
Section |
Category |
| CIS, Russia, Ukraine |
Structural steel |
Low alloy structural steel for welded structures |
Chemical composition
| Standard |
Fe, % |
Si, % |
Mn, % |
Cr, % |
As, % |
P, % |
C, % |
S, % |
|---|
| GOST 10884-94 |
95.52–96.94 |
1.6–2.2 |
0.6–0.9 |
0.6–0.9 |
< 0.08 |
< 0.04 |
0.26–0.32 |
< 0.04 |
Information on suppliers
Mechanical properties at 20 °C
| Rolling |
Standard |
Size, mm |
Tension |
Classifiers |
$$\sigma _{U}$$, $$MPa$$ |
$$\sigma_{P}$$, $$MPa$$ |
$$\epsilon_L$$, % |
Treatment |
|---|
| Round |
GOST 10884-71 |
Ø 10–14 |
|
|
1420 |
1175 |
6 |
|
| Round |
GOST 10884-71 |
Ø 16–32 |
|
|
1370 |
1175 |
5 |
|
Technological Properties
Standards
Description of chemical elements
| Element |
Units of measurement |
Description |
| Fe |
% |
Iron |
| Si |
% |
Silicon |
| Mn |
% |
Manganese |
| Cr |
% |
Chrome |
| As |
% |
Arsenic |
| P |
% |
Phosphorus |
| C |
% |
Carbon |
| S |
% |
Sulfur |
Description of mechanical properties
| Parameter |
Units of measurement |
Description |
| $$\sigma _{U}$$ |
$$MPa$$ |
Ultimate tensile strength |
| $$\sigma_{P}$$ |
$$MPa$$ |
Proportionality limit |
| $$\epsilon_L$$ |
% |
Elongation at break (longitudinal) |
Designation of types of weldability
| Parameter |
Units of measurement |
Description |
| no limits |
|
Welding is performed without heating and without subsequent heat treatment |
| Boundedly welded |
|
Welding is possible with heating up to 100–120 °C and subsequent heat treatment |
| Difficult to weld |
|
For obtaining quality welded joints, additional operations are required: heating up to 200–300 °C for welding, heat treatment after welding — annealing |
| Not applicable for welded structures |
|
|