Alloy 33NK-VI
for soldering with soft glass S72−4, for connection with ceramic and mica; 1000000 * TFLE at temperatures ranging from -70 to +450 ºC to 6 — 9 [1 / ºC]
Classification
| Country |
Section |
Category |
| CIS, Russia, Ukraine |
Precision alloys |
With given TCLE |
Chemical composition
| Standard |
Fe, % |
Si, % |
Mn, % |
Co, % |
Ni, % |
P, % |
C, % |
S, % |
O, % |
N, % |
H, % |
|---|
| GOST 10994-74 |
48.221–51 |
< 0.3 |
< 0.4 |
16.5–17.5 |
32.5–33.5 |
< 0.015 |
< 0.03 |
< 0.015 |
< 0.008 |
< 0.01 |
< 0.001 |
Information on suppliers
Physical characteristics
| Temperature, °C |
$$E\cdot 10^{9}$$, $$MPa$$ |
$$\rho$$, $$\frac{kg}{m^3}$$ |
$$R\cdot 10^{-6}$$, $$\Omega\cdot m$$ |
|---|
| 20 |
142 |
8200 |
420 |
Mechanical properties at 20 °C
| Rolling |
Standard |
Size, mm |
Tension |
Classifiers |
$$\sigma _{U}$$, $$MPa$$ |
$$\sigma_{Y}$$, $$MPa$$ |
d5, % |
Treatment |
|---|
| The tape is hardcore. |
GOST 14086-68 |
100 |
Transverse |
|
920–950 |
600–650 |
10–15 |
|
Magnetic properties
| Rolling |
$$\mu_{max}$$, $$MH/m$$ |
$$B_{10000}$$, $$T$$ |
|---|
| The tape is hardcore. |
> 40000 |
< 15000 |
Brinell hardness number
| Rolling |
Standard |
Classifiers |
Value, HBW |
| The tape is hardcore. |
GOST 14086-68 |
|
230–250 |
Casting and technological parameters
Limit operating modes
| Standard |
Температура, °C |
|---|
|
< 450 |
Properties
| Property |
|---|
| Сплав производится вакуумно-индукционной плавкой |
Standards
Description of chemical elements
| Element |
Units of measurement |
Description |
| Fe |
% |
Iron |
| Si |
% |
Silicon |
| Mn |
% |
Manganese |
| Co |
% |
Cobalt |
| Ni |
% |
Nickel |
| P |
% |
Phosphorus |
| C |
% |
Carbon |
| S |
% |
Sulfur |
| O |
% |
Oxygen |
| N |
% |
Nitrogen |
| H |
% |
Hydrogen |
Description of physical characteristics
| Parameter |
Units of measurement |
Description |
| $$E\cdot 10^{9}$$ |
$$MPa$$ |
Elastic modulus |
| $$\rho$$ |
$$\frac{kg}{m^3}$$ |
The density of the material |
| $$R\cdot 10^{-6}$$ |
$$\Omega\cdot m$$ |
Electrical resistivity |
Description of mechanical properties
| Parameter |
Units of measurement |
Description |
| d5 |
% |
Elongation at break |
| $$\sigma_{Y}$$ |
$$MPa$$ |
Yield strength |
| $$\sigma _{U}$$ |
$$MPa$$ |
Ultimate tensile strength |
Description of magnetic properties
| Parameter |
Units of measurement |
Description |
| $$\mu_{max}$$ |
$$MH/m$$ |
Magnetic permeability (not more) |
| $$B_{10000}$$ |
$$T$$ |
Magnetic induction (not less) in a magnetic field while magnetic field strength is 10000 A/m |
Description of the casting and technological parameters
| Parameter |
Units of measurement |
Description |
| melting point |
°C |
The temperature at which solid crystalline body makes the transition to the liquid state and Vice versa |