35g
Tie rods, axes, earrings, beams, levers, clutches, shafts, sprockets, cylinders, wheels, spindles, couplings of steam turbines, nuts, bolts, screws and other parts, which are requirements of low strength.
Tie rods, axes, earrings, beams, levers, clutches, shafts, sprockets, cylinders, wheels, spindles, couplings of steam turbines, nuts, bolts, screws and other parts, which are requirements of low strength.
Standard | Fe, % | Si, % | Mn, % | Cr, % | Cu, % | Ni, % | P, % | C, % | S, % |
---|---|---|---|---|---|---|---|---|---|
Standard | Fe, % | Si, % | Mn, % | Cr, % | Cu, % | Ni, % | P, % | C, % | S, % |
GOST 4543-71 | 97.26–98.81 | 0.17–0.37 | 0.7–1 | < 0.3 | < 0.3 | < 0.3 | < 0.035 | 0.32–0.4 | < 0.035 |
Rolling | Standard | Size, mm | Tension | Classifiers | \sigma _{U}, MPa | \sigma_{P}, MPa | \epsilon_L, % | \psi, % | KCU\cdot 10^{3}, \frac{J}{m^2} | Treatment |
---|---|---|---|---|---|---|---|---|---|---|
Rolling | Standard | Size, mm | Tension | Classifiers | \sigma _{U}, MPa | \sigma_{P}, MPa | \epsilon_L, % | \psi, % | KCU\cdot 10^{3}, \frac{J}{m^2} | Treatment |
Rod | GOST 4543-71 | 25 | 570 | 340 | 18 | 45 | 700 | Tempering 860 ° C, the water, leave 600 ° C, air |
Rolling | Standard | Classifiers | Value, HBW |
---|---|---|---|
Rolling | Standard | Classifiers | Value, HBW |
Alloy | GOST 4543-71 | annealing | 207 |
Standard | Description |
---|---|
Standard | Description |
GOST 4543-71 |
Parameter | Units of measurement | Description |
---|---|---|
Parameter | Units of measurement | Description |
\sigma _{U} | MPa | Ultimate tensile strength |
\sigma_{P} | MPa | Proportionality limit |
\epsilon_L | % | Elongation at break (longitudinal) |
\psi | % | Reduction in cross section on fracture |
KCU\cdot 10^{3} | \frac{J}{m^2} | Impact toughness |