35HMFA
For the manufacture of forgings of various general machinery parts
For the manufacture of forgings of various general machinery parts
Standard | Fe, % | Si, % | Mn, % | Cr, % | Ti, % | Cu, % | Ni, % | V, % | P, % | C, % | S, % | Mo, % | W, % |
---|---|---|---|---|---|---|---|---|---|---|---|---|---|
Standard | Fe, % | Si, % | Mn, % | Cr, % | Ti, % | Cu, % | Ni, % | V, % | P, % | C, % | S, % | Mo, % | W, % |
TU 14-1-950-74 | 95.92–97.83 | 0.17–0.37 | 0.4–0.7 | 1–1.3 | < 0.03 | < 0.25 | < 0.3 | 0.1–0.2 | < 0.025 | 0.3–0.38 | < 0.025 | 0.2–0.3 | < 0.2 |
Rolling | Standard | Size, mm | Tension | Classifiers | \sigma _{U}, MPa | \sigma_{Y}, MPa | \psi, % | KCU\cdot 10^{3}, \frac{J}{m^2} | d5, % | Treatment |
---|---|---|---|---|---|---|---|---|---|---|
Rolling | Standard | Size, mm | Tension | Classifiers | \sigma _{U}, MPa | \sigma_{Y}, MPa | \psi, % | KCU\cdot 10^{3}, \frac{J}{m^2} | d5, % | Treatment |
Rod | TU 14-1-950-74 | Ø 25 | 1080 | 930 | 50 | 885 | 10 |
Standard | Description |
---|---|
Standard | Description |
TU 14-1-950-74 |