40H2N2MA (40Х1НВА)

Major products: shafts, wheels, gear pinions, and fasteners.

Classification

Country	Section	Category
Country	Section	Category
CIS, Russia, Ukraine	Structural steel	Alloyed structural steel

Chemical composition

Standard	Fe, %	Si, %	Mn, %	Cr, %	Cu, %	Ni, %	P, %	C, %	S, %	Mo, %
Standard	Fe, %	Si, %	Mn, %	Cr, %	Cu, %	Ni, %	P, %	C, %	S, %	Mo, %
GOST 4543-71	94.56–96.38	0.17–0.37	0.3–0.6	1.25–1.65	< 0.3	1.35–1.75	< 0.025	0.35–0.42	< 0.025	0.2–0.3

Information on suppliers

Wish to advertise here?

Mechanical properties at 20 °C

Rolling	Standard	Size, mm	Tension	Classifiers	$\sigma _{U}$ , $MPa$	$\sigma_{P}$ , $MPa$	$\epsilon_L$ , %	$\psi$ , %	$KCU\cdot 10^{3}$ , $\frac{J}{m^2}$	Treatment
Rolling	Standard	Size, mm	Tension	Classifiers	$\sigma _{U}$ , $MPa$	$\sigma_{P}$ , $MPa$	$\epsilon_L$ , %	$\psi$ , %	$KCU\cdot 10^{3}$ , $\frac{J}{m^2}$	Treatment
Rod	GOST 4543-71	25			1080	930	10	45	780	Hardening and tempering

Brinell hardness number

Rolling	Standard	Classifiers	Value, HBW
Rolling	Standard	Classifiers	Value, HBW
Alloy	GOST 4543-71	annealing	255

Technological Properties

Weldability	Flake Susceptibility	Propensity to temper brittleness
Weldability	Flake Susceptibility	Propensity to temper brittleness
Difficult to weld	sensitive	not inclined

Critical point temperatures

Ac₁, K	Ac₃(Ac_m), K
Ac₁, K	Ac₃(Ac_m), K
740	805

Analogues

USA	Germany
USA	Germany
H43400	1.6565 (40NiCrMo6)

Standards

Standard	Description
Standard	Description
GOST 4543-71

Description of chemical elements

Element	Units of measurement	Description
Element	Units of measurement	Description
Fe	%	Iron
Si	%	Silicon
Mn	%	Manganese
Cr	%	Chrome
Cu	%	Copper
Ni	%	Nickel
P	%	Phosphorus
C	%	Carbon
S	%	Sulfur
Mo	%	Molybdenum

Description of mechanical properties

Parameter	Units of measurement	Description
Parameter	Units of measurement	Description
$\sigma _{U}$	$MPa$	Ultimate tensile strength
$\sigma_{P}$	$MPa$	Proportionality limit
$\epsilon_L$	%	Elongation at break (longitudinal)
$\psi$	%	Reduction in cross section on fracture
$KCU\cdot 10^{3}$	$\frac{J}{m^2}$	Impact toughness

Designation of types of weldability

Parameter	Units of measurement	Description
Parameter	Units of measurement	Description
no limits		Welding is performed without heating and without subsequent heat treatment
Boundedly welded		Welding is possible with heating up to 100–120 °C and subsequent heat treatment
Difficult to weld		For obtaining quality welded joints, additional operations are required: heating up to 200–300 °C for welding, heat treatment after welding — annealing
Not applicable for welded structures

Description of temperatures of critical points

Parameter	Units of measurement	Description
Parameter	Units of measurement	Description
Ac₁	K
Ac₃(Ac_m)	K