60HG
Steel is not used for welded structures, prone to temper embrittlement. Flock sensitivity: sensitive. Temperature of critical points: Ac1 = 750, Ac3 (Acm) = 800, Mn = 250. Hardness after normalization and tempering: HB 10 -1 = 229 — 285 MPa. Hardness after quenching and tempering: HB 10 -1 = 255 — 302 MPa. Substitute: 55X .
shtripsovyh work rolls and small-section mill for hot rolling of metals.
Classification
| Country |
Section |
Category |
| CIS, Russia, Ukraine |
Tool steel |
Roll tool steel |
Chemical composition
| Standard |
Fe, % |
Si, % |
Mn, % |
Cr, % |
Ni, % |
P, % |
C, % |
S, % |
|---|
| OST 24.013.21 - 0 |
96.2–97.48 |
0.17–0.37 |
0.8–1 |
1–1.3 |
< 0.4 |
< 0.04 |
0.55–0.65 |
< 0.04 |
Information on suppliers
Mechanical properties at 20 °C
| Rolling |
Standard |
Size, mm |
Tension |
Classifiers |
$$\sigma _{U}$$, $$MPa$$ |
$$\sigma_{P}$$, $$MPa$$ |
$$\epsilon_L$$, % |
$$\psi$$, % |
$$KCU\cdot 10^{3}$$, $$\frac{J}{m^2}$$ |
Treatment |
|---|
| Rolls |
|
< 600 |
|
|
800–910 |
440–550 |
18 |
38 |
350 |
|
Brinell hardness number
| Rolling |
Standard |
Classifiers |
Value, HBW |
| Alloy |
|
normalization, average vacation |
229–285 |
| Alloy |
|
Hardening, average vacation |
255–302 |
Technological Properties
| Weldability |
Flake Susceptibility |
Propensity to temper brittleness |
|---|
| Not applicable for welded structures |
sensitive |
inclined |
Critical point temperatures
| Ac1, K |
Ac3(Acm), K |
Mn, K |
|---|
| 750 |
800 |
250 |
Standards
Description of chemical elements
| Element |
Units of measurement |
Description |
| Fe |
% |
Iron |
| Si |
% |
Silicon |
| Mn |
% |
Manganese |
| Cr |
% |
Chrome |
| Ni |
% |
Nickel |
| P |
% |
Phosphorus |
| C |
% |
Carbon |
| S |
% |
Sulfur |
Description of mechanical properties
| Parameter |
Units of measurement |
Description |
| $$\sigma _{U}$$ |
$$MPa$$ |
Ultimate tensile strength |
| $$\sigma_{P}$$ |
$$MPa$$ |
Proportionality limit |
| $$\epsilon_L$$ |
% |
Elongation at break (longitudinal) |
| $$\psi$$ |
% |
Reduction in cross section on fracture |
| $$KCU\cdot 10^{3}$$ |
$$\frac{J}{m^2}$$ |
Impact toughness |
Designation of types of weldability
| Parameter |
Units of measurement |
Description |
| no limits |
|
Welding is performed without heating and without subsequent heat treatment |
| Boundedly welded |
|
Welding is possible with heating up to 100–120 °C and subsequent heat treatment |
| Difficult to weld |
|
For obtaining quality welded joints, additional operations are required: heating up to 200–300 °C for welding, heat treatment after welding — annealing |
| Not applicable for welded structures |
|
|
Description of temperatures of critical points
| Parameter |
Units of measurement |
Description |
| Ac1 |
K |
|
| Ac3(Acm) |
K |
|
| Mn |
K |
|