60S2 (60S2A)

Responsible and heavy duty springs and springs. Not applicable for welded structures.

Substitute: 55S2, 50HFA.

Heavy duty springs, torsion bars, spring rings, collets, friction discs, spring washers.

Classification

Country	Section	Category
Country	Section	Category
CIS, Russia, Ukraine	Structural steel	Spring-spring structural steel

Chemical composition

Standard	Fe, %	Si, %	Mn, %	Cr, %	Cu, %	Ni, %	P, %	C, %	S, %
Standard	Fe, %	Si, %	Mn, %	Cr, %	Cu, %	Ni, %	P, %	C, %	S, %
GOST 14959-79	95.63–97.33	1.5–2	0.6–0.9	< 0.3	< 0.2	< 0.25	< 0.035	0.57–0.65	< 0.035

Information on suppliers

Wish to advertise here?

Physical characteristics

Temperature, °C	$E\cdot 10^{9}$ , $MPa$	$\alpha\cdot 10^{6}$ , $K^{-1}$	$\varkappa$ , $\frac{W}{m\cdot K}$	$\rho$ , $\frac{kg}{m^3}$	$c\cdot 10^{-3}$ , $\frac{J}{kg\cdot K}$
Temperature, °C	$E\cdot 10^{9}$ , $MPa$	$\alpha\cdot 10^{6}$ , $K^{-1}$	$\varkappa$ , $\frac{W}{m\cdot K}$	$\rho$ , $\frac{kg}{m^3}$	$c\cdot 10^{-3}$ , $\frac{J}{kg\cdot K}$
20	2.12		28	7680
100	2.06	11.8	29	7660	0.51
200	1.98	12.7	29	7630	0.51
300	1.92	13.3	30	7590	0.52
400	1.81	13.7	30	7570	0.535
500	1.78	14.1	30	7520	0.565
600	1.58	14.5	29		0.585
700	1.44	14.4	29		0.62
800	1.34	12.2	28		0.7

Mechanical properties at 20 °C

Rolling	Standard	Size, mm	Tension	Classifiers	$\sigma _{U}$ , $MPa$	$\sigma_{P}$ , $MPa$	$\psi$ , %	d5, %	Treatment
Rolling	Standard	Size, mm	Tension	Classifiers	$\sigma _{U}$ , $MPa$	$\sigma_{P}$ , $MPa$	$\psi$ , %	d5, %	Treatment
Hire	GOST 14959-79				1270	1175	25	6	Tempering 870 ° C, oil, leave 470 ° C
The tape is annealed.				annealing	900			8

Brinell hardness number

Rolling	Standard	Classifiers	Value, HBW
Rolling	Standard	Classifiers	Value, HBW
Alloy	GOST 14959-79	annealing	269
Alloy	GOST 14959-79		302

Technological Properties

Weldability	Flake Susceptibility	Propensity to temper brittleness
Weldability	Flake Susceptibility	Propensity to temper brittleness
Not applicable for welded structures	not sensitive	not inclined

Critical point temperatures

Ac₁, K	Ac₃(Ac_m), K	Ar₃(Arc_m), K	Ar₁, K	Mn, K
Ac₁, K	Ac₃(Ac_m), K	Ar₃(Arc_m), K	Ar₁, K	Mn, K
770	820	770	700	305

Analogues

USA	Germany	European Union
USA	Germany	European Union
H92600	1.7108 (60SiCr7)	60Si7

Standards

Standard	Description
Standard	Description
GOST 14959-79

Description of chemical elements

Element	Units of measurement	Description
Element	Units of measurement	Description
Fe	%	Iron
Si	%	Silicon
Mn	%	Manganese
Cr	%	Chrome
Cu	%	Copper
Ni	%	Nickel
P	%	Phosphorus
C	%	Carbon
S	%	Sulfur

Description of physical characteristics

Parameter	Units of measurement	Description
Parameter	Units of measurement	Description
$E\cdot 10^{9}$	$MPa$	Elastic modulus
$\alpha\cdot 10^{6}$	$K^{-1}$	Coefficient of thermal (linear) expansion (range 20°C–T)
$\varkappa$	$\frac{W}{m\cdot K}$	Coefficient of thermal conductivity (the heat capacity of the material)
$\rho$	$\frac{kg}{m^3}$	The density of the material
$c\cdot 10^{-3}$	$\frac{J}{kg\cdot K}$	The specific heat of the material (range 20°C–T)

Description of mechanical properties

Parameter	Units of measurement	Description
Parameter	Units of measurement	Description
d5	%	Elongation at break
$\sigma _{U}$	$MPa$	Ultimate tensile strength
$\sigma_{P}$	$MPa$	Proportionality limit
$\psi$	%	Reduction in cross section on fracture

Designation of types of weldability

Parameter	Units of measurement	Description
Parameter	Units of measurement	Description
no limits		Welding is performed without heating and without subsequent heat treatment
Boundedly welded		Welding is possible with heating up to 100–120 °C and subsequent heat treatment
Difficult to weld		For obtaining quality welded joints, additional operations are required: heating up to 200–300 °C for welding, heat treatment after welding — annealing
Not applicable for welded structures

Description of temperatures of critical points

Parameter	Units of measurement	Description
Parameter	Units of measurement	Description
Ac₁	K
Ac₃(Ac_m)	K
Ar₃(Arc_m)	K
Ar₁	K
Mn	K