95NLM-VI (EI996M)

The alloy precipitation hardens corrosion with low specific resistivity ≤0.42 Ohm mm 2 / m.

Used for the production of the tape, sanded rods (silverfish) and wire for the manufacture of a conductive and elastic force sensing elements Aviapribor and other devices operating at temperatures up to 300 ° C.

Classification

Country Section Category
CIS, Russia, Ukraine Precision alloys With preset elastic properties

Chemical composition

Standard Fe, % Si, % B, % Be, % Ca, % Mn, % Ni, % P, % C, % S, % Mo, %
TU 14-1-436-72 < 0.3 < 0.2 < 0.0025 2–2.4 < 0.05 < 0.2 90.7775–93 < 0.01 < 0.05 < 0.01 5–6

Information on suppliers

Mechanical properties at 20 °C

Rolling Standard Size, mm Tension Classifiers \sigma _{U}, MPa \sigma_{0.2}, MPa δ, % d5, % Treatment
Tape TU 14-1-436-72 < 1079 < 589 > 25 Tape according to TU 14-1-436-72 after quenching in water with 1080 ± 10 ° C
Tape TU 14-1-436-72 > 1373 > 1030 > 15
Tape TU 14-1-436-72 > 1864 > 1472 > 11 Tape according to TU 14-1-436-72 after quenching in water with 1080 ± 10 ° C, 35% slander and dispersion hardening at 550 ± 10 ° C (extraction 1.5-2.0 h)
Wire TU 14-1-436-72 > 1080 > 7 Tape according to TU 14-1-436-72 after quenching in water with 1080 ± 10 ° C, 35% slander and dispersion hardening at 550 ± 10 ° C (extraction 1.5-2.0 h)

Standards

Standard Description
TU 14-1-436-72

Description of chemical elements

Element Units of measurement Description
Fe % Iron
Si % Silicon
B % Bor
Be % Beryllium
Ca % Calcium
Mn % Manganese
Ni % Nickel
P % Phosphorus
C % Carbon
S % Sulfur
Mo % Molybdenum

Description of mechanical properties

Parameter Units of measurement Description
δ % Elongation after rupture
d5 % Elongation at break
\sigma_{0.2} MPa Tensile stress required to produce a total elongation of 0.2%
\sigma _{U} MPa Ultimate tensile strength