AD31 (1310)

For the manufacture of parts of low strength and high corrosion resistance, working in range from -70 to 50 deg.

Classification

Country Section Category
CIS, Russia, Ukraine Aluminum, aluminum alloys Wrought Aluminum Alloys

Chemical composition

Standard Fe, % Si, % Mg, % Mn, % Cr, % Ti, % Cu, % Zn, % Al, %
GOST 4784-97 < 0.5 0.2–0.6 0.45–0.9 < 0.1 < 0.1 < 0.15 < 0.1 < 0.2 97.65–99.35

Information on suppliers

Physical characteristics

Temperature, °C $$E\cdot 10^{9}$$, $$MPa$$ $$\alpha\cdot 10^{6}$$, $$K^{-1}$$ $$\varkappa$$, $$\frac{W}{m\cdot K}$$ $$\rho$$, $$\frac{kg}{m^3}$$ $$c\cdot 10^{-3}$$, $$\frac{J}{kg\cdot K}$$ $$R\cdot 10^{-6}$$, $$\Omega\cdot m$$
20 71 2710 0.0344
100 23.4 188 0.921

Mechanical properties at 20 °C

Rolling Standard Size, mm Tension Classifiers $$\sigma _{U}$$, $$MPa$$ $$\sigma_{P}$$, $$MPa$$ $$\epsilon_L$$, % Treatment
Trumpet 130 60 12
Trumpet 180 120 10
Round GOST 21488-97 90 60 15
Round GOST 21488-97 135–195 70–145 8–13
Profile < 100 196 147 10
Profile 127 69 13

Brinell hardness number

Rolling Standard Classifiers Value, HBW
Hardening, aging 80

Analogues

Germany USA
3.2316 AA6060

Standards

Standard Description
GOST 4784-97

Description of chemical elements

Element Units of measurement Description
Fe % Iron
Si % Silicon
Mg % Magnesium
Mn % Manganese
Cr % Chrome
Ti % Titan
Cu % Copper
Zn % Zinc
Al % Aluminium

Description of physical characteristics

Parameter Units of measurement Description
$$E\cdot 10^{9}$$ $$MPa$$ Elastic modulus
$$\alpha\cdot 10^{6}$$ $$K^{-1}$$ Coefficient of thermal (linear) expansion (range 20°C–T)
$$\varkappa$$ $$\frac{W}{m\cdot K}$$ Coefficient of thermal conductivity (the heat capacity of the material)
$$\rho$$ $$\frac{kg}{m^3}$$ The density of the material
$$c\cdot 10^{-3}$$ $$\frac{J}{kg\cdot K}$$ The specific heat of the material (range 20°C–T)
$$R\cdot 10^{-6}$$ $$\Omega\cdot m$$ Electrical resistivity

Description of mechanical properties

Parameter Units of measurement Description
$$\sigma _{U}$$ $$MPa$$ Ultimate tensile strength
$$\sigma_{P}$$ $$MPa$$ Proportionality limit
$$\epsilon_L$$ % Elongation at break (longitudinal)