BrOF6.5-0.4

Wire mesh for paper machines; for springs, machine parts, ribbons and strips used in mechanical

Classification

Country Section Category
CIS, Russia, Ukraine Bronze Pressure Tin Bronze

Chemical composition

Standard Fe, % Si, % Sn, % Bi, % Cu, % Zn, % Ni, % Sb, % Al, % Pb, % P, %
GOST 5017-2006 < 0.02 < 0.005 6–7 < 0.002 92.15–93.64 < 0.3 < 0.2 < 0.002 < 0.002 < 0.02 0.26–0.4

Information on suppliers

Physical characteristics

Temperature, °C E109, MPa α106, K1 ϰ, WmK ρ, kgm3 R106, Ωm
20 112 71.4 8700 0.16
100 17.1

Mechanical properties at 20 °C

Rolling Standard Size, mm Tension Classifiers σU, MPa ϵL, % Treatment
Alloy soft 300–450 60–70
Alloy solid 700–800 7–10

Brinell hardness number

Rolling Standard Classifiers Value, HBW
Alloy soft 700–900
Alloy solid 170–220

Casting and technological parameters

melting point, °C Hot working temperature, °C annealing temperature, °C
995 700–800 600–650

Coefficients of Friction

coefficient of friction with lubrication coefficient of friction without lubrication
0.01 0.12

Standards

Standard Description
GOST 5017-2006 Wrought tin bronzes. Grades

Description of chemical elements

Element Units of measurement Description
Fe % Iron
Si % Silicon
Sn % Tin
Bi % Bismuth
Cu % Copper
Zn % Zinc
Ni % Nickel
Sb % Antimony
Al % Aluminium
Pb % Lead
P % Phosphorus

Description of physical characteristics

Parameter Units of measurement Description
E109 MPa Elastic modulus
α106 K1 Coefficient of thermal (linear) expansion (range 20°C–T)
ϰ WmK Coefficient of thermal conductivity (the heat capacity of the material)
ρ kgm3 The density of the material
R106 Ωm Electrical resistivity

Description of mechanical properties

Parameter Units of measurement Description
σU MPa Ultimate tensile strength
ϵL % Elongation at break (longitudinal)

Description of the casting and technological parameters

Parameter Units of measurement Description
melting point °C The temperature at which solid crystalline body makes the transition to the liquid state and Vice versa
Hot working temperature °C The temperature at which the plastic-deformed metal recrystallizes during the pressure treatment
annealing temperature °C The temperature at which the processes return recrystallization and homogenization of the metal to reduce its hardness for subsequent machining