| Standard | Fe, % | Si, % | Mn, % | Cr, % | Ni, % | Al, % | P, % | C, % | S, % | N, % |
|---|---|---|---|---|---|---|---|---|---|---|
| Standard | Fe, % | Si, % | Mn, % | Cr, % | Ni, % | Al, % | P, % | C, % | S, % | N, % |
| TU 14-3-917-80 | 70.13–73.17 | 1.8–2.2 | 11–12 | 12–13 | 1.8–2.2 | 0.05–0.15 | < 0.03 | 0.08–0.12 | < 0.02 | 0.1–0.15 |
| Property |
|---|
| Property |
| Pipes according to TU 14-3-917-80 After austenization Outer diameter: 32 - 42 mm; Wall thickness: 4 - 6 mm; Yield Strength:> 372 MPa |
| Pipes according to TU 14-3-917-80 After austenization Outer diameter: 32 - 42 mm; Wall thickness: 4 - 6 mm; Temporary resistance:> 784 MPa |
| Pipes according to TU 14-3-917-80 After austenization Outer diameter: 32 - 42 mm; Wall thickness: 4 - 6 mm; Elongation:> 35% |
| Calculated Properties Density: 7.63 g / cm3 |
| Standard | Description |
|---|---|
| Standard | Description |
| TU 14-3-917-80 |