| Standard | Fe, % | Si, % | Mn, % | Cr, % | Ni, % | V, % | P, % | C, % | S, % | Mo, % |
|---|---|---|---|---|---|---|---|---|---|---|
| Standard | Fe, % | Si, % | Mn, % | Cr, % | Ni, % | V, % | P, % | C, % | S, % | Mo, % |
| TU 14-1-2573-78 | 74.85–78.85 | < 0.5 | < 0.5 | 11–12 | 7.8–8.6 | 0.05–0.7 | < 0.01 | < 0.03 | < 0.01 | 2.3–2.8 |
| Property |
|---|
| Property |
| Products according to TU 14-1-2573-78 Yield strength: 850 MPa |
| Products according to TU 14-1-2573-78 Temporary resistance: 970 MPa |
| Products according to TU 14-1-2573-78 Elongation: 12% |
| Products according to TU 14-1-2573-78 Impact strength KCU at 20 ° C: 120 J / cm2 |
| Products according to TU 14-1-2573-78 Relative contraction: 55% |
| Physical properties Density: 7.85 g / cm3 |
| Note Two-phase (duplex) stainless steel |
| Standard | Description |
|---|---|
| Standard | Description |
| TU 14-1-2573-78 |