DI70-MP
Classification
Chemical composition
| Standard | Fe, % | Si, % | Mn, % | Cr, % | Ni, % | Ce, % | P, % | C, % | S, % | Nb, % | Mo, % | W, % |
|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Standard | Fe, % | Si, % | Mn, % | Cr, % | Ni, % | Ce, % | P, % | C, % | S, % | Nb, % | Mo, % | W, % |
| TU 14-3-1093-82 | 17.445–27.07 | < 0.6 | 1.2–2 | 20–22 | 44–48 | < 0.05 | < 0.02 | 0.03–0.07 | < 0.015 | 0.9–1.3 | 4–5 | 2.8–3.5 |
Information on suppliers
Properties
| Property |
|---|
| Property |
| Pipes according to TU 14-3-1093-82 After austenization and stabilization Outer diameter: 13 - 60 mm; Wall thickness: 1.5 - 6.0 mm; Yield Strength:> 343 MPa |
| Pipes according to TU 14-3-1093-82 After austenization and stabilization Outer diameter: 13 - 60 mm; Wall thickness: 1.5 - 6.0 mm; Temporary resistance:> 686 MPa |
| Pipes according to TU 14-3-1093-82 After austenization and stabilization Outer diameter: 13 - 60 mm; Wall thickness: 1.5 - 6.0 mm; Elongation:> 30% |
| Calculated Properties Density: 8.64 g / cm3 |
Standards
| Standard | Description |
|---|---|
| Standard | Description |
| TU 14-3-1093-82 |