| Hot-deformed pipes according to TU 14-3-1892-93 Normalization Outer diameter: 108 - 325 mm; Wall thickness: 6 - 30 mm; Yield Strength:> 490 MPa |
| Hot-deformed pipes according to TU 14-3-1892-93 Normalization Outer diameter: 108 - 325 mm; Wall thickness: 6 - 30 mm; Temporary resistance:> 343 MPa |
| Hot-deformed pipes according to TU 14-3-1892-93 Normalization Outer diameter: 108 - 325 mm; Wall thickness: 6 - 30 mm; Elongation:> 17% |
| Hot-deformed pipes according to TU 14-3-1892-93 Normalization Outer diameter: 108 - 325 mm; Wall thickness: 6 - 30 mm; Impact strength KCV at 20 ° C:> 98 |
| Vacation Outer Diameter: 16 - 89 mm; Wall thickness: 2.5 - 8.0 mm; Yield Strength:> 490 MPa |
| Vacation Outer Diameter: 16 - 89 mm; Wall thickness: 2.5 - 8.0 mm; Temporary resistance:> 343 MPa |
| Vacation Outer Diameter: 16 - 89 mm; Wall thickness: 2.5 - 8.0 mm; Elongation:> 20% |
| Cold-deformed pipes according to TU 14-3-1412-86 Normalization Outer diameter: 108 - 325 mm; Wall thickness: 6 - 30 mm; Vacation Outer Diameter: 16 - 89 mm; Wall thickness: 2.5 - 8.0 mm; Yield Strength:> 490 MPa |
| Cold-deformed pipes according to TU 14-3-1412-86 Normalization Outer diameter: 108 - 325 mm; Wall thickness: 6 - 30 mm; Vacation Outer Diameter: 16 - 89 mm; Wall thickness: 2.5 - 8.0 mm; Temporary resistance:> 343 M |
| Cold-deformed pipes according to TU 14-3-1412-86 Normalization Outer diameter: 108 - 325 mm; Wall thickness: 6 - 30 mm; Vacation Outer Diameter: 16 - 89 mm; Wall thickness: 2.5 - 8.0 mm; Elongation:> 20% |
| Sheets according to TU 14-1-3946-85 Normalization with tempering Cross-section: 2 - 30 mm; Yield Strength:> 540 MPa |
| Sheets according to TU 14-1-3946-85 Normalization with tempering Cross-section: 2 - 30 mm; Temporary resistance:> 343 MPa |
| Sheets according to TU 14-1-3946-85 Normalization with tempering Cross-section: 2 - 30 mm; Elongation:> 20% |
| Sheets according to TU 14-1-3946-85 Normalization with tempering Cross-section: 2 - 30 mm; Impact strength KCV at 20 ° C:> 59 J / cm2 |
| Sheet, forgings according to TU 0900-006-057644-17-99 Normalization with tempering Section: 10 - 160 mm; Yield Strength:> 600 MPa |
| Sheet, forgings according to TU 0900-006-057644-17-99 Normalization with tempering Section: 10 - 160 mm; Temporary resistance:> 400 MPa |
| Sheet, forgings according to TU 0900-006-057644-17-99 Normalization with tempering Section: 10 - 160 mm; Elongation:> 20% |
| Sheet, forgings according to TU 0900-006-057644-17-99 Normalization with tempering Section: 10 - 160 mm; Relative narrowing:> 55% |
| Sheet, forgings according to TU 0900-006-057644-17-99 Normalization with tempering Section: 10 - 160 mm; Impact strength KCV at 20 ° C:> 59 J / cm2 |
| Tempering with tempering Cross-section: <600 mm; Yield Strength:> 600 MPa |
| Tempering with tempering Cross-section: <600 mm; Temporary resistance:> 400 MPa |
| Tempering with tempering Cross-section: <600 mm; Elongation:> 20% |
| Tempering with tempering Cross-section: <600 mm; Relative narrowing:> 55% |
| Tempering with tempering Cross-section: <600 mm; Impact strength KCV at 20 ° C:> 59 J / cm2 |
| Pipe billets according to TU 14-134-319-93 Normalization with tempering Cross-section: 90 - 180 mm; Yield Strength:> 600 MPa |
| Pipe billets according to TU 14-134-319-93 Normalization with tempering Cross-section: 90 - 180 mm; Temporary resistance:> 400 MPa |
| Pipe billets according to TU 14-134-319-93 Normalization with tempering Cross-section: 90 - 180 mm; Elongation:> 20% |
| Pipe billets according to TU 14-134-319-93 Normalization with tempering Cross-section: 90 - 180 mm; Relative narrowing:> 55% |
| Pipe billets according to TU 14-134-319-93 Normalization with tempering Cross-section: 90 - 180 mm; Impact strength KCV at 20 ° C:> 59 J / cm2 |
| Physical properties Critical temperature of brittleness, Тк10: -40 - -10 ° С |
| Physical properties Linear expansion coefficient: 11.5 (10 ^ 6) / ° С |
| Performance data Application temperature: <610 ° C |
| Calculated properties Density: 7.8 g / cm3 |