| According to OST 5P.9125-84 Yield strength:> 412 MPa Tensile strength:> 589 MPa Hardness HB: 147 - 217 |
| Tape according to GOST 4986 Soft tape Note At the request of the consumer, a tape elongation of 0.5 mm or less is allowed to reduce elongation by 2%. |
| Tape according to GOST 4986 Soft tape Thickness: <0.2 mm; Temporary resistance:> 440 MPa |
| Tape according to GOST 4986 Soft tape Thickness: <0.2 mm; Elongation:> 9% |
| Tape according to GOST 4986 Soft tape Thickness: 0.2 - 2.0 mm; Temporary resistance:> 440 MPa |
| Tape according to GOST 4986 Soft tape Thickness: 0.2 - 2.0 mm; Elongation:> 17% |
| Sheet metal in accordance with GOST 5582 After softening heat treatment Temporary resistance:> 440 MPa |
| Sheet metal according to GOST 5582 After softening heat treatment Elongation:> 21% |
| Products according to GOST 5949 Note Yield strength:> 410 MPa |
| Products according to GOST 5949 Note Temporary resistance:> 590 MPa |
| Products according to GOST 5949 Note Elongation:> 20% |
| Products according to GOST 5949 Note Hardness HB: 121 - 197 |
| Products according to GOST 5949 Note Impact strength KCU at 20 ° C:> 88 J / cm2 |
| Products according to GOST 5949 Note Relative contraction:> 60% |
| Products according to GOST 5949 Note Fingerprint diameter: 4.4 - 5.4 mm |
| Plate rolling according to GOST 7350 Yield strength:> 345 MPa |
| Plate rolling according to GOST 7350 Temporary resistance:> 490 MPa |
| Plate rolling according to GOST 7350 Elongation:> 21% |
| Manufacturer Annealing Yield Strength:> 250 MPa |
| Manufacturer's annealing Temporary resistance: <650 MPa |
| Manufacturer mode anneal Elongation:> 15% |
| Pipes according to GOST 9940 Temporary resistance:> 392 MPa |
| Pipes according to GOST 9940 Elongation:> 21% |
| Pipes according to GOST 9940 Density: 7.7 g / cm3 |
| Pipes according to GOST 9941 Temporary resistance:> 392 MPa |
| Pipes according to GOST 9941 Elongation:> 22% |
| Pipes according to GOST 9941 Density: 7.7 g / cm3 |
| Wire according to GOST 18143 Heat-treated products Class 1 Diameter: 1 - 6 mm; Temporary resistance: 490 - 740 MPa |
| Wire according to GOST 18143 Heat-treated products Class 1 Diameter: 1 - 6 mm; Elongation:> 20% |
| Wire according to GOST 18143 Heat-treated products Class 2 Diameter: 1 - 6 mm; Temporary resistance: 490 - 740 MPa |
| Wire according to GOST 18143 Heat-treated products Class 2 Diameter: 1 - 6 mm; Elongation:> 16% |
| Bars in accordance with GOST 18907 Heat-treated products Heat-treated for a given strength (TP) Temporary resistance: 490 - 780 MPa |
| Rods according to GOST 18907 Heat-treated products Heat-treated for a given strength (TP) Elongation:> 16% |
| Bars in accordance with GOST 18907 Heat-treated products At the request of the consumer (optional) Diameter: 4 - 8 mm; Temporary resistance: 568 - 764 MPa |
| Bars in accordance with GOST 18907 Heat-treated products Bars in accordance with GOST 18907 Heat-treated products At the request of the consumer (optional) Diameter: 4 - 8 mm; Elongation: 16% |
| Bars in accordance with GOST 18907 Heat-treated products At the request of the consumer (optional) Diameter:> 8 mm; Temporary resistance:> 568 MPa |
| Bars in accordance with GOST 18907 Heat-treated products At the request of the consumer (optional) Diameter:> 8 mm; Elongation:> 16% |
| Bars in accordance with GOST 18907 Annealed (T) Diameter:> 5 mm; Hardness HB: 121 - 187 |
| Bars in accordance with GOST 18907 Annealed (T) Diameter:> 5 mm; Imprint Diameter: 4.4 - 5.4 mm |
| Products according to GOST 18968 Heat-treated samples Bars Diameter: <16 mm; Yield Strength: 440 - 610 MPa |
| Products according to GOST 18968 Heat-treated samples Bars Diameter: <16 mm; Temporary resistance:> 620 MPa |
| Products according to GOST 18968 Heat-treated samples Bars Diameter: <16 mm; Elongation:> 20% |
| Products according to GOST 18968 Heat-treated samples Bars Diameter: <16 mm; Hardness HB: 192 - 229 |
| Products according to GOST 18968 Heat-treated samples Bars Diameter: <16 mm; Imprint Diameter: 4.00 - 4.35 mm |
| Products in accordance with GOST 19442 Note For bars with a thickness of more than 60 mm, a relative elongation of 1% is allowed. |
| Products according to GOST 19442 Thickness: <60 mm; Temporary resistance: 617 - 784 MPa |
| Products according to GOST 19442 Thickness: <60 mm; Elongation:> 20% |
| Products according to GOST 19442 Thickness: <60 mm; Hardness HB: 187 - 229 |
| Products according to GOST 19442 Thickness: <60 mm; Strength Category: KP42 |
| Products according to GOST 19442 Thickness: <60 mm; Imprint Diameter: 4.0 - 4.4 mm |
| Products according to GOST 19442 Hardness standards apply to all shaped rods for blades and to rods for connecting blades with the largest width (diameter) of more than 10 mm. |
| Products according to GOST 19442 Thickness: <60 mm; Yield Strength: 441 - 607 MPa |
| Products according to GOST 19442 Thickness: <60 mm; Temporary resistance:> 617 MPa |
| Products according to GOST 19442 Thickness: <60 mm; Elongation:> 20% |
| Products according to GOST 19442 Thickness: <60 mm; Hardness HB: 187 - 229 |
| Products according to GOST 19442 Thickness: <60 mm; KCU impact strength at 20 ° C:> 78.4 J / cm2 |
| Products according to GOST 19442 Thickness: <60 mm; Strength Category: KP42 |
| Products according to GOST 19442 Thickness: <60 mm; Relative narrowing:> 60% |
| Products according to GOST 19442 Thickness: <60 mm; Imprint Diameter: 4.0 - 4.4 mm |
| Products according to GOST 25054 Note Mechanical properties of groups IV, IVK, V, VK and hardness of all groups except I. |
| Products according to GOST 25054 Diameter: <200 mm; Yield Strength:> 392 MPa |
| Products according to GOST 25054 Diameter: <200 mm; Temporary resistance:> 617 MPa |
| Products according to GOST 25054 Diameter: <200 mm; Elongation:> 18% |
| Products according to GOST 25054 Diameter: <200 mm; Hardness HB: 187 - 229 |
| Products according to GOST 25054 Diameter: <200 mm Impact strength KCU at 20 ° C:> 7.5 J / cm2 |
| Products according to GOST 25054 Diameter: <200 mm; Relative contraction:> 50% |
| Products according to GOST 25054 Diameter: 200 - 500 mm; Yield Strength:> 392 MPa |
| Products according to GOST 25054 Diameter: 200 - 500 mm; Temporary resistance:> 617 MPa |
| Products according to GOST 25054 Diameter: 200 - 500 mm; Elongation:> 16% |
| Products in accordance with GOST 25054 Diameter: 200 - 500 mm; Hardness HB: 187 - 229 |
| Products according to GOST 25054 Diameter: 200 - 500 mm; Impact strength KCU at 20 ° C:> 6 J / cm2 |
| Products according to GOST 25054 Diameter: 200 - 500 mm; Relative narrowing:> 44% |
| Products according to GOST 25054 Diameter: 500 - 1000 mm; Yield Strength:> 392 MPa |
| Products according to GOST 25054 Diameter: 500 - 1000 mm; Temporary resistance:> 617 MPa |
| Products according to GOST 25054 Diameter: 500 - 1000 mm; Elongation:> 15% |
| Products in accordance with GOST 25054 Diameter: 500 - 1000 mm; Hardness HB: 187 - 229 |
| Products according to GOST 25054 Diameter: 500 - 1000 mm; Impact strength KCU at 20 ° C:> 5 J / cm2 |
| Products according to GOST 25054 Diameter: 500 - 1000 mm; Relative narrowing:> 40% |
| Blanks for turbine blades according to OST 108.020.03-82 Tempering with tempering Yield strength: 539 - 686 MPa |
| Blanks for turbine blades according to OST 108.020.03-82 Tempering with tempering Temporary resistance:> 686 MPa |
| Blanks for turbine blades according to OST 108.020.03-82 Tempering with tempering Elongation:> 15% |
| Blanks for turbine blades according to OST 108.020.03-82 Tempering with tempering Hardness HB: 217 - 255 |
| Blanks for turbine blades according to OST 108.020.03-82 Tempering with tempering Impact strength KCU at 20 ° C:> 58 J / cm2 |
| Blanks for turbine blades according to OST 108.020.03-82 Tempering with tempering Elongation:> 15% Tw |
| Blanks for turbine blades according to OST 108.020.03-82 Forgings according to OST 108.958.04-85 Strength category KP40 Longitudinal samples Thickness: <300 mm; Yield Strength:> 390 MPa |
| Blanks for turbine blades according to OST 108.020.03-82 Forgings according to OST 108.958.04-85 Strength category KP40 Longitudinal samples Thickness: <300 mm; Temporary resistance:> 615 MPa |
| Blanks for turbine blades according to OST 108.020.03-82 Forgings according to OST 108.958.04-85 Strength category KP40 Longitudinal samples Thickness: <300 mm; Elongation:> 15% |
| Blanks for turbine blades according to OST 108.020.03-82 Forgings according to OST 108.958.04-85 Strength category KP40 Longitudinal samples Thickness: <300 mm; Hardness HB: 187 - 229 |
| Blanks for turbine blades according to OST 108.020.03-82 Forgings according to OST 108.958.04-85 Strength category KP40 Longitudinal samples Thickness: <300 mm; Impact strength KCU at 20 ° C:> 49 J / cm2 |
| Blanks for turbine blades according to OST 108.020.03-82 Forgings according to OST 108.958.04-85 Strength category KP40 Longitudinal samples Thickness: <300 mm; Relative narrowing:> 40% |
| According to TU 3600-010-88626180-2012 Strength class K42 Yield strength:> 245 MPa |
| According to TU 3600-010-88626180-2012 Strength class K42 Temporary resistance:> 412 MPa |
| According to TU 3600-010-88626180-2012 Strength class K42 Elongation:> 21% |
| According to TU 3600-010-88626180-2012 Strength class K46 Yield strength:> 274 MPa |
| According to TU 3600-010-88626180-2012 Strength class K46 Temporary resistance:> 451 MPa |
| According to TU 3600-010-88626180-2012 Strength class K46 Relative elongation:> 21% |
| According to TU 3600-010-88626180-2012 Strength class K48 Yield strength:> 305 MPa Tensile strength:> 471 MPa Elongation:> 21% |
| According to TU 3600-010-88626180-2012 Strength class K52 Yield strength:> 353 MPa Tensile strength:> 510 MPa Elongation:> 20% |
| According to TU 3600-010-88626180-2012 Strength class K54 Yield strength:> 373 MPa Tensile strength:> 530 MPa Elongation:> 20% |
| According to TU 3600-010-88626180-2012 Strength class K56 Yield strength:> 392 MPa Tensile strength:> 549 MPa Elongation:> 19% |
| According to TU 3600-010-88626180-2012 Strength class K60 Yield strength:> 441 MPa Tensile strength:> 589 MPa Elongation:> 19% |
| Operational characteristics According to GOST R 54803-2011 Sheet Application temperature: -40 - 550 ° C |
| Operational characteristics According to GOST R 54803-2011 Forgings Application temperature: -40 - 550 ° C |
| Operational characteristics According to GOST R 54803-2011 Long products Application temperature: -40 - 550 ° C |
| Performance characteristics According to STO 00220227-006-2010 Application temperature: -40 - 550 ° C |
| Operational characteristics According to ST TsKBA 025-2006 Application temperature: -40 - 420 ° C |
| According to OST 5P.9125-84 By thickness Note Continuous section: diameter (thickness) Hollow section: wall thickness |
| According to OST 5P.9125-84 Thickness Diameter or thickness: <60 mm; Wall thickness: <50 mm; Relative elongation:> 20% Impact strength KCU at 20 ° C:> 90 J / cm2 Relative narrowing:> 60% |
| According to OST 5P.9125-84 Thickness Diameter or thickness: 60 - 100 mm; Wall thickness: 50 - 80 mm; Elongation:> 19% Impact strength KCU at 20 ° C:> 80 J / cm2 Elongation:> 55% |
| According to OST 5P.9125-84 Diameter or thickness: 100 - 300 mm; Wall thickness: 80 - 210 mm; Elongation:> 17% Impact strength KCU at 20 ° C:> 60 J / cm2 Elongation:> 50% |
| Note Heat Resistant Steel Corrosion Resistant Steel Martensitic Ferritic Steel Heat Resistant Steel |