| Billets according to OST 108.961.05-80 / 87 VD Rotors Strength category KP60 Longitudinal samples Temporary resistance:> 736 MPa Elongation:> 13% |
| Billets according to OST 108.961.05-80 / 87 VD Rotors Strength category KP60 Longitudinal samples Impact strength KCU at 20 ° C:> 49 J / cm2 Relative narrowing:> 40% Conditional yield strength: 589 - 736 MPa |
| Billets according to OST 108.961.05-80 / 87 VD Rotors Tangential samples Test temperature 20 ° C Temporary resistance:> 716 MPa Elongation:> 11% Impact strength KCU at 20 ° C:> 39 J / cm2 |
| Billets according to OST 108.961.05-80 / 87 VD Rotors Tangential samples Test temperature 20 ° C Relative narrowing:> 32% Conditional yield strength: 589 - 736 MPa |
| Billets according to OST 108.961.05-80 / 87 VD Rotors Tangential samples Test temperature 400 ° C Conditional yield strength:> 539 MPa |
| Billets according to OST 108.961.05-80 / 87 VD Rotors Strength category KP65 Tangential samples Test temperature 20 ° C Temporary resistance:> 736 MPa Elongation:> 11% Impact strength KCU at 20 ° C:> 39 J / cm2 |
| Billets according to OST 108.961.05-80 / 87 VD Rotors Strength category KP65 Tangential samples Test temperature 20 ° C Relative narrowing:> 32% Conditional yield strength: 615 - 765 MPa |
| Billets according to OST 108.961.05-80 / 87 VD Rotors Test temperature 400 ° C Conditional yield strength:> 549 MPa |
| Billets according to OST 108.961.05-80 / 87 VD Disks KP70 strength category Tangential samples Test temperature 20 ° C Temporary resistance:> 785 MPa Elongation:> 13% Impact strength KCU at 20 ° C:> 49 J / cm2 |
| Billets according to OST 108.961.05-80 / 87 VD Disks KP70 strength category Tangential samples Test temperature 20 ° C Relative narrowing:> 40% Conditional yield strength: 647 - 795 MPa |
| Billets according to OST 108.961.05-80 / 87 VD Disks KP70 strength category Tangential samples Test temperature 550 ° C Conditional yield strength:> 392 MPa |
| Tests at elevated temperature According to OST 108.020.109-82 Temperature: 200 ° C; Yield Strength:> 542 MPa |
| Tests at elevated temperature According to OST 108.020.109-82 Temperature: 400 ° C; Yield Strength:> 473 MPa |
| OST 108.020.109-82 Temperature: 500 ° C; Yield strength:> 443 MPa; Long-term tensile strength per 100,000 h: 207 - 266 MPa; Creep strength corresponding to 1% of the total deformation per 100,000 h: 118 - 167 MPa |
| Temperature: 550 ° C; Yield strength:> 394 MPa; Long-term tensile strength per 100,000 h: 148 - 158 MPa; Creep strength corresponding to 1% of the total deformation per 100,000 h: 89 - 108 MPa |
| Tests at elevated temperature According to OST 108.020.109-82 Temperature: 600 ° C; Yield Strength:> 345 MPa |
| Calculated Properties Density: 7.87 g / cm3 |