| Weldability By NAKS Group: M51 (W51) |
| Typical Specifications Temperature: 20 ° C; Yield strength: 650 - 750 MPa; Temporary resistance: 1050 - 1150 MPa; Elongation: 12 - 28% |
| Typical Specifications Temperature: 20 ° C; Relative narrowing: 15 - 30% Impact strength An at 20 ° C: 50 - 80 J / cm2 |
| Typical Specifications Temperature: 700 ° C; Yield strength: 600 - 700 MPa Tensile strength: 900 - 1000 MPa Elongation: 15 - 30% Elongation: 15 - 32% |
| Typical characteristics Temperature: 700 ° С Long-term strength for 100h: 480 - 520 MPa Long-term strength for 10,000h: 300 - 320 MPa Long-term strength for 500h: 410 - 430 MPa Impact strength An at 700 ° C: 60 - 100 J / cm2 |
| Typical characteristics Temperature: 700 ° С Long-term strength for 1000 h: 370 - 390 MPa Long-term strength for 300 h: 420 - 550 MPa |
| Typical Specifications Temperature: 750 ° C; Yield strength: 550 - 650 MPa; Temporary resistance: 750 - 850 MPa; Elongation: 6 - 23%; Relative narrowing: 9 - 25% |
| Typical characteristics Temperature: 750 ° С Long-term strength for 100 h: 370 - 400 MPa Long-term strength for 10000 h: 200 - 220 MPa Long-term strength for 500 h: 300 - 320 MPa |
| Typical characteristics Temperature: 750 ° С Impact strength An at 750 ° C: 50 - 100 J / cm2 Long-term strength for 1000 h: 280 - 300 MPa Long-term strength for 300 h: 320 - 340 MPa |
| Typical Specifications Temperature: 800 ° C; Yield strength: 500 - 620 MPa; Temporary resistance: 700 - 800 MPa; Elongation: 6 - 18%; Relative narrowing: 9 - 20% |
| Typical characteristics Temperature: 800 ° С Long-term strength for 100 h: 280 - 300 MPa Long-term strength for 10000 h: 130 - 150 MPa Long-term strength for 500 h: 200 - 230 MPa |
| Typical characteristics Temperature: 800 ° С Impact strength An at 800 ° C: 70 - 120 J / cm2 Long-term strength for 1000 h: 180 - 200 MPa Long-term strength for 300 h: 230 - 250 MPa |
| Typical Specifications Temperature: 850 ° C; Yield strength: 470 - 580 MPa; Temporary resistance: 550 - 650 MPa; Elongation: 8 - 20%; Relative narrowing: 10 - 15% |
| Typical Specifications Temperature: 850 ° C; Long-term strength for 100 h: 180 - 200 MPa Long-term strength for 10000 h: 70 - 80 MPa Long-term strength for 500 h: 120 - 140 MPa |
| Typical characteristics Temperature: 850 ° С; Long-term strength for 1000 h: 110 - 130 MPa Long-term strength for 300 h: 140 - 160 MPa Impact strength An at 850 ° C: 80 - 140 J / cm2 |
| Typical Specifications Temperature: 900 ° C; Yield strength: 380 - 450 MPa; Temporary resistance: 420 - 550 MPa; Elongation: 15 - 25%; Relative contraction: 20 - 30% |
| Typical Specifications Temperature: 900 ° C; Long-term strength for 100 h: 120 - 140 MPa Long-term strength for 10000 h: 40 - 45 MPa Long-term strength for 500 h: 80 - 90 MPa |
| Typical characteristics Temperature: 900 ° С Long-term strength for 1000 h: 65 - 75 MPa Long-term strength for 300 h: 90 - 100 MPa Impact strength An at 900 ° C: 80 - 150 J / cm2 |
| Typical Specifications Temperature: 950 ° C; Long-term strength for 100 h: 60 - 70 MPa Long-term strength for 500 h: 40 - 45 MPa |
| Typical characteristics Temperature: 950 ° С Long-term strength for 1000 h: 35 MPa Long-term strength for 300 h: 45 - 55 MPa |
| Calculated Properties Density: 8.83 g / cm3 |