EI467 (50H)

Classification

Country Section Category
CIS, Russia, Ukraine Corrosion-resistant alloys and steels Corrosion-resistant heat-resistant steel

Chemical composition

Standard Fe, % Si, % Mn, % Cu, % Ni, % P, % C, % S, %
48.33–50.55 0.15–0.3 0.3–0.6 < 0.2 49–50.5 < 0.02 < 0.03 < 0.02

Information on suppliers

Wish to advertise here?

Properties

Property
Products according to GOST10160 Heat-treated samples Class I Cold-rolled steel Tape Thickness: 0.05 mm; Coercive force: <20 A / m Initial magnetic permeability:> 2.5 mH / m
Products according to GOST10160 Heat-treated samples Class I Cold-rolled steel Tape Thickness: 0.05 mm Maximum magnetic permeability:> 25 mH / m Technical saturation induction:> 1.5 T
Products according to GOST10160 Heat-treated samples Class I Cold-rolled steel Tape Thickness: 0.08 mm; Coercive force: <20 A / m Initial magnetic permeability:> 2.5 mH / m
Products according to GOST10160 Heat-treated samples Class I Cold-rolled steel Tape Thickness: 0.08 mm Maximum magnetic permeability:> 25 mH / m Technical saturation induction:> 1.5 T
Products according to GOST10160 Heat-treated samples Class I Cold-rolled steel Tape Thickness: 0.1 mm; Coercive force: <16 A / m Initial magnetic permeability:> 2.9 mH / m
Products according to GOST10160 Heat-treated samples Class I Cold-rolled steel Tape Thickness: 0.1 mm; Maximum magnetic permeability:> 31 mH / m Technical saturation induction:> 1.5 T
Thickness: 0.15 mm; Coercive force: <16 A / m Initial magnetic permeability:> 2.9 mH / m Maximum magnetic permeability:> 31 mH / m Technical saturation induction:> 1.5 T
Thickness: 0.2 mm; Coercive force: <12 A / m Initial magnetic permeability:> 3.3 mH / m Maximum magnetic permeability:> 38 mH / m Technical saturation induction:> 1.5 T
Thickness: 0.25 - 0.27 mm; Coercive force: <12 A / m Initial magnetic permeability:> 3.3 mH / m Maximum magnetic permeability:> 38 mH / m Technical saturation induction:> 1.5 T
Thickness: 0.35 mm; Coercive force: <10 A / m Initial magnetic permeability:> 3.8 mH / m Maximum magnetic permeability:> 44 mH / m Technical saturation induction:> 1.5 T
Thickness: 0.5mm; Coercive force: <10 A / m Initial magnetic permeability:> 3.8 mH / m Maximum magnetic permeability:> 44 mH / m Technical saturation induction:> 1.5 T
Thickness: 0.8 mm; Coercive force: <12 A / m Initial magnetic permeability:> 3.8 mH / m Maximum magnetic permeability:> 38 mH / m Technical saturation induction:> 1.5 T
Thickness: 1 mm; Coercive force: <12 A / m Initial magnetic permeability:> 3.8 mH / m Maximum magnetic permeability:> 38 mH / m Technical saturation induction:> 1.5 T
Thickness: 1.5 mm; Coercive force: <13 A / m Initial magnetic permeability:> 3.5 mH / m Maximum magnetic permeability:> 31 mH / m Technical saturation induction:> 1.5 T
Thickness: 2 mm; Coercive force: <13 A / m Initial magnetic permeability:> 3.5 mH / m Maximum magnetic permeability:> 31 mH / m Technical saturation induction:> 1.5 T
Thickness: 2.5 mm; Coercive force: <13 A / m Initial magnetic permeability:> 3.5 mH / m Maximum magnetic permeability:> 31 mH / m Technical saturation induction:> 1.5 T
Hot Rolled Steel Sheet Thickness: 3 - 22 mm; Coercive force: <24 A / m Initial magnetic permeability:> 3.1 mH / m
Hot Rolled Steel Sheet Thickness: 3 - 22 mm; Maximum magnetic permeability:> 25 mH / m Technical saturation induction:> 1.5 T
Bars Class II Cold-rolled steel Tape:
Thickness: 0.1 mm; Coercive force: <14 A / m Initial magnetic permeability:> 3.8 mH / m Maximum magnetic permeability:> 38 mH / m Technical saturation induction:> 1.5 T
Thickness: 0.15 mm; Coercive force: <14 A / m Initial magnetic permeability:> 3.8 mH / m Maximum magnetic permeability:> 38 mH / m Technical saturation induction:> 1.5 T
Thickness: 0.2 mm; Coercive force: <12 A / m Initial magnetic permeability:> 4.4 mH / m Maximum magnetic permeability:> 44 mH / m Technical saturation induction:> 1.5 T
Thickness: 0.25 mm; Coercive force: <12 A / m Initial magnetic permeability:> 4.4 mH / m Maximum magnetic permeability:> 44 mH / m Technical saturation induction:> 1.5 T
Thickness: 0.35 mm; Coercive force: <10 A / m Initial magnetic permeability:> 5 mH / m Maximum magnetic permeability:> 56 mH / m Technical saturation induction:> 1.5 T
Thickness: 0.5mm; Coercive force: <10 A / m Initial magnetic permeability:> 5 mH / m Maximum magnetic permeability:> 56 mH / m Technical saturation induction:> 1.5 T
Thickness: 0.8 mm; Coercive force: <10 A / m Initial magnetic permeability:> 5 mH / m Maximum magnetic permeability:> 50 mH / m Technical saturation induction:> 1.5 T
Thickness: 1 mm; Coercive force: <10 A / m Initial magnetic permeability:> 5 mH / m Maximum magnetic permeability:> 50 mH / m Technical saturation induction:> 1.5 T
Thickness: 1.5 mm; Coercive force: <12 A / m Initial magnetic permeability:> 3.8 mH / m Maximum magnetic permeability:> 44 mH / m Technical saturation induction:> 1.5 T
Thickness: 2 mm; Coercive force: <12 A / m Initial magnetic permeability:> 3.8 mH / m Maximum magnetic permeability:> 44 mH / m Technical saturation induction:> 1.5 T
Class III Cold-rolled steel Tape Note Magnetic permeability is given for a field of 0.4 A / m
Class III Cold Rolled Tape
Thickness: 0.05 mm; Coercive force: <4 A / m Initial magnetic permeability:> 12.5 mH / m Maximum magnetic permeability:> 75 mH / m Technical saturation induction:> 1.52 T
Thickness: 0.1 mm; Coercive force: <4 A / m Initial magnetic permeability:> 12.5 mH / m Maximum magnetic permeability:> 75 mH / m Technical saturation induction:> 1.52 T
Thickness: 0.2 mm; Coercive force: <4 A / m Initial magnetic permeability:> 12.5 mH / m Maximum magnetic permeability:> 75 mH / m Technical saturation induction:> 1.52 T
Calculated Properties Density: 8.37 g / cm3
Calculated Properties Density: 8.37 g / cm3
EI467 / Aloro

Description of chemical elements

Element Units of measurement Description
Fe % Iron
Si % Silicon
Mn % Manganese
Cu % Copper
Ni % Nickel
P % Phosphorus
C % Carbon
S % Sulfur