| Standard | Fe, % | Si, % | Mn, % | Cr, % | Cu, % | Ni, % | P, % | C, % | S, % |
|---|---|---|---|---|---|---|---|---|---|
| Standard | Fe, % | Si, % | Mn, % | Cr, % | Cu, % | Ni, % | P, % | C, % | S, % |
| OST 108.961.04-80 / 87 ВД | 83.765–87.5 | 0.3–0.6 | 0.2–0.7 | 12–14 | < 0.3 | < 0.5 | < 0.03 | < 0.08 | < 0.025 |
| Property |
|---|
| Property |
| Castings according to OST 108.961.04-80 / 87 VD Temporary resistance:> 392 MPa Elongation:> 20% |
| Castings according to OST 108.961.04-80 / 87 VD Impact strength KCU at 20 ° C:> 39 J / cm2 Relative narrowing:> 40% Conditional yield strength:> 196 MPa |
| Calculated Properties Density: 7.76 g / cm3 |
| Germany | USA |
|---|---|
| Germany | USA |
| 1.4000 (X6Cr13) | S41008 |
| Standard | Description |
|---|---|
| Standard | Description |
| OST 108.961.04-80 / 87 ВД |