EI539LMU (HN65VKMBYUTL)
Classification
| Country |
Section |
Category |
| CIS, Russia, Ukraine |
Corrosion-resistant alloys and steels |
Corrosion-resistant heat-resistant steel |
Chemical composition
| Standard |
Fe, % |
Si, % |
B, % |
Mn, % |
Co, % |
Cr, % |
Ti, % |
Ni, % |
Al, % |
Ce, % |
P, % |
C, % |
S, % |
Nb, % |
Y, % |
Mo, % |
W, % |
|---|
| TU 108.02.058-82 |
< 1 |
< 0.3 |
0.02 |
< 0.3 |
4–6 |
15.7–17.1 |
2.2–3 |
58.855–68.54 |
3.2–4 |
0.02 |
< 0.015 |
0.08–0.14 |
< 0.01 |
1.2–1.8 |
0.04 |
1.5–2.4 |
3.5–5 |
Information on suppliers
Properties
| Property |
|---|
| Workpiece according to TU 108.1118-82 Tensile strength:> 784 MPa Elongation:> 3% Impact strength KCU at 20 ° C:> 15 J / cm2 |
| Workpiece according to TU 108.1118-82 Long-term strength Test temperature 800 ° C Long-term strength for 100 h: 412 MPa |
| Workpiece according to TU 108.1118-82 Long-term strength Test temperature 850 ° C Long-term strength for 100 h: 294 MPa |
| Blades according to TU 108.02.058-82 Temporary resistance:> 726 MPa Elongation:> 3% |
| Blades according to TU 108.02.058-82 Long-term strength Test temperature: 850 ° C; Tensile strength per 100h: 294 MPa |
| Blades according to TU 108.02.059-82 Temporary resistance:> 726 MPa Elongation:> 3% |
| Blades according to TU 108.02.059-82 Long-term strength Test temperature: 850 ° C; Tensile strength per 100h: 294 MPa |
| Calculated Properties Density: 8.71 g / cm3 |
| Note Cast gas turbine blades |
Standards
Description of chemical elements
| Element |
Units of measurement |
Description |
| Fe |
% |
Iron |
| Si |
% |
Silicon |
| B |
% |
Bor |
| Mn |
% |
Manganese |
| Co |
% |
Cobalt |
| Cr |
% |
Chrome |
| Ti |
% |
Titan |
| Ni |
% |
Nickel |
| Al |
% |
Aluminium |
| Ce |
% |
Cerium |
| P |
% |
Phosphorus |
| C |
% |
Carbon |
| S |
% |
Sulfur |
| Nb |
% |
Niobium |
| Y |
% |
Yttrium |
| Mo |
% |
Molybdenum |
| W |
% |
Tungsten |