EI572-VD (31X19H9MVBT-VD)

Country	Section	Category
Country	Section	Category
CIS, Russia, Ukraine	Corrosion-resistant alloys and steels	Corrosion-resistant alloys

Standard	Fe, %	Si, %	Mn, %	Cr, %	Ti, %	Cu, %	Ni, %	P, %	C, %	S, %	Nb, %	Mo, %	W, %
Standard	Fe, %	Si, %	Mn, %	Cr, %	Ti, %	Cu, %	Ni, %	P, %	C, %	S, %	Nb, %	Mo, %	W, %
OST 108.961.05-80	61.85–69.67	< 0.8	0.65–1.65	18–20	0.2–0.5	< 0.3	9–11	< 0.03	0.28–0.35	< 0.02	0.2–0.5	1–1.5	1–1.5

Property
Property
OST blanks 108.961.05-80 Application temperature: <600 ° C
OST blanks 108.961.05-80 Rotors Strength category KP35 Longitudinal samples Tensile strength:> 667 MPa Elongation:> 25% Impact strength KCU at 20 ° C:> 59 J / cm2
Billets according to OST 108.961.05-80 Rotors Strength category KP35 Longitudinal samples Relative narrowing:> 25% Conditional yield strength:> 343 MPa
OST blanks 108.961.05-80 Rotors Strength category KP35 Tangential samples Tensile strength:> 667 MPa Elongation:> 20% Impact strength KCU at 20 ° C:> 49 J / cm2
OST blanks 108.961.05-80 Rotors Strength category KP35 Tangential samples Relative narrowing:> 20% Conditional yield strength:> 343 MPa
OST blanks 108.961.05-80 Wheels KP35 strength category Longitudinal samples Tensile strength:> 667 MPa Elongation:> 25% KCU impact strength at 20 ° C:> 59 J / cm2
OST blanks 108.961.05-80 Discs KP35 strength category Longitudinal samples Relative narrowing:> 25% Conditional yield strength:> 343 MPa
OST blanks 108.961.05-80 Discs KP35 strength category Tangential samples Test temperature 20 ° C Temporary resistance:> 667 MPa Elongation:> 20% Impact strength KCU at 20 ° C:> 49 J / cm2
OST blanks 108.961.05-80 Discs KP35 strength category Tangential samples Test temperature 20 ° C Relative narrowing:> 20% Yield strength:> 343 MPa
OST blanks 108.961.05-80 Discs KP35 strength category Tangential samples Test temperature 600 ° C Conditional yield strength:> 245 MPa
Calculated Properties Density: 7.95 g / cm3

USA
USA
S63199