EI612K (HN35KWT)
Classification
| Country |
Section |
Category |
| CIS, Russia, Ukraine |
Corrosion-resistant alloys and steels |
Corrosion-resistant heat-resistant steel |
Chemical composition
| Standard |
Fe, % |
Si, % |
B, % |
Mn, % |
Co, % |
Cr, % |
Ti, % |
Ni, % |
Al, % |
P, % |
C, % |
S, % |
W, % |
|---|
| TU 14-1-272-72 |
33.25–43.5 |
< 0.5 |
< 0.01 |
1–2 |
3.5–4.5 |
14–16 |
1.2–1.6 |
34–38 |
< 0.5 |
< 0.02 |
< 0.1 |
< 0.02 |
2.8–3.5 |
Information on suppliers
Properties
| Property |
|---|
| According to TU 14-1-272-72 Yield strength:> 345 MPa Tensile strength:> 590 MPa Elongation:> 15% |
| According to TU 14-1-272-72 Impact strength KCU at 20 ° C:> 68.6 J / cm2 Relative narrowing:> 35% |
| Reference characteristics Elastic modulus (Young's modulus): 193 GPa Density: 8.2 g / cm3 Linear expansion coefficient: 14.8 - 16.5 (10 ^ 6) / ° С |
| Reference characteristics Tempering with tempering Yield strength:> 350 MPa Tensile strength:> 650 MPa Elongation:> 15% |
| Reference characteristics Tempering with vacation |
| Reference characteristics Aging Yield strength:> 400 MPa Tensile strength:> 750 MPa Elongation:> 15% |
| Reference characteristics Aging Hardness HB: 229 Impact strength KCU at 20 ° C:> 50 J / cm2 Relative narrowing:> 25% |
| Note Parts operating at temperatures up to 700 ° C. Old version of the standard. |
Standards
Description of chemical elements
| Element |
Units of measurement |
Description |
| Fe |
% |
Iron |
| Si |
% |
Silicon |
| B |
% |
Bor |
| Mn |
% |
Manganese |
| Co |
% |
Cobalt |
| Cr |
% |
Chrome |
| Ti |
% |
Titan |
| Ni |
% |
Nickel |
| Al |
% |
Aluminium |
| P |
% |
Phosphorus |
| C |
% |
Carbon |
| S |
% |
Sulfur |
| W |
% |
Tungsten |