| Standard | Fe, % | Si, % | Mn, % | Cr, % | Ti, % | Ni, % | Al, % | P, % | C, % | S, % |
|---|---|---|---|---|---|---|---|---|---|---|
| Standard | Fe, % | Si, % | Mn, % | Cr, % | Ti, % | Ni, % | Al, % | P, % | C, % | S, % |
| TU 14-1-1531-76 | 61.16–69.7 | < 1 | < 1 | 10–12.5 | 2.3–2.8 | 18–21 | < 0.4 | < 0.02 | < 0.1 | < 0.02 |
| Property |
|---|
| Property |
| Typical characteristics Test temperature 20 ° C Yield strength:> 450 MPa Tensile strength:> 800 MPa Elongation:> 15% |
| Typical characteristics Relative narrowing:> 15% Imprint diameter: 3.5 - 3.9 mm Impact strength An at 20 ° C:> 30 J / cm2 |
| Typical characteristics Test temperature 700 ° C Long-term strength for 30 h:> 400 MPa |
| Calculated Properties Density: 7.85 g / cm3 |
| Standard | Description |
|---|---|
| Standard | Description |
| TU 14-1-1531-76 | |
| TU 14-1-2918-80 |