EP495 (H70M)
Classification
| Country |
Section |
Category |
| CIS, Russia, Ukraine |
Nickel, nickel alloys |
Low alloyed nickel alloys |
Chemical composition
| Standard |
Fe, % |
Si, % |
Mn, % |
Cr, % |
Ni, % |
P, % |
C, % |
S, % |
Mo, % |
|---|
|
< 1.5 |
< 0.25 |
< 0.5 |
< 0.3 |
68.375–75 |
< 0.025 |
< 0.03 |
< 0.02 |
25–29 |
Information on suppliers
Physical characteristics
| Temperature, °C |
$$E\cdot 10^{9}$$, $$MPa$$ |
$$\alpha\cdot 10^{6}$$, $$K^{-1}$$ |
$$\varkappa$$, $$\frac{W}{m\cdot K}$$ |
Cp, Дж/кг·К |
|---|
| 20 |
217 |
10.3 |
11.1 |
377 |
Mechanical properties at 20 °C
| Rolling |
Standard |
Size, mm |
Tension |
Classifiers |
$$\sigma _{U}$$, $$MPa$$ |
$$\sigma_{Y}$$, $$MPa$$ |
d5, % |
Treatment |
|---|
| Tape |
|
100 |
Transverse |
|
745 |
325 |
40 |
|
Brinell hardness number
| Rolling |
Standard |
Classifiers |
Value, HBW |
| Tape |
|
|
< 250 |
Casting and technological parameters
| melting point, °C |
|---|
| 1330–1380 |
Technological Properties
| Weldability |
Flake Susceptibility |
Propensity to temper brittleness |
|---|
| no limits |
not sensitive |
loathsome |
Properties
| Property |
|---|
| transitional alloy with incomplete austenitic structure |
Analogues
Description of chemical elements
| Element |
Units of measurement |
Description |
| Fe |
% |
Iron |
| Si |
% |
Silicon |
| Mn |
% |
Manganese |
| Cr |
% |
Chrome |
| Ni |
% |
Nickel |
| P |
% |
Phosphorus |
| C |
% |
Carbon |
| S |
% |
Sulfur |
| Mo |
% |
Molybdenum |
Description of physical characteristics
| Parameter |
Units of measurement |
Description |
| Cp |
Дж/кг·К |
Specific heat of material |
| $$E\cdot 10^{9}$$ |
$$MPa$$ |
Elastic modulus |
| $$\alpha\cdot 10^{6}$$ |
$$K^{-1}$$ |
Coefficient of thermal (linear) expansion (range 20°C–T) |
| $$\varkappa$$ |
$$\frac{W}{m\cdot K}$$ |
Coefficient of thermal conductivity (the heat capacity of the material) |
Description of mechanical properties
| Parameter |
Units of measurement |
Description |
| d5 |
% |
Elongation at break |
| $$\sigma_{Y}$$ |
$$MPa$$ |
Yield strength |
| $$\sigma _{U}$$ |
$$MPa$$ |
Ultimate tensile strength |
Description of the casting and technological parameters
| Parameter |
Units of measurement |
Description |
| melting point |
°C |
The temperature at which solid crystalline body makes the transition to the liquid state and Vice versa |
Designation of types of weldability
| Parameter |
Units of measurement |
Description |
| no limits |
|
Welding is performed without heating and without subsequent heat treatment |
| Boundedly welded |
|
Welding is possible with heating up to 100–120 °C and subsequent heat treatment |
| Difficult to weld |
|
For obtaining quality welded joints, additional operations are required: heating up to 200–300 °C for welding, heat treatment after welding — annealing |
| Not applicable for welded structures |
|
|