HA30 (ZhS30-VI)
Production of cast bar stock for further refining during casting of blades and other shaped castings
Classification
| Country | Section | Category |
|---|---|---|
| CIS, Russia, Ukraine | Heat resistant steels and alloys | Heat resistant alloys |
Chemical composition
| Standard | Fe, % | Si, % | B, % | Ca, % | Mn, % | Co, % | Cr, % | Ti, % | Ni, % | Zr, % | Al, % | Ce, % | P, % | C, % | S, % | Nb, % | La, % | Y, % | Mo, % | W, % | Hf, % |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| OST 1-90126 - 85 | < 1 | < 0.4 | < 0.02 | < 0.005 | < 0.4 | 7.5–9.5 | 5–9 | 1.4–2.3 | 55.08–69.09 | < 0.02 | 4.8–5.8 | < 0.015 | < 0.015 | 0.11–0.2 | < 0.01 | 0.4–1.4 | < 0.005 | < 0.03 | 0.4–1 | 11–12.6 | 0.3–1.2 |
Information on suppliers
Mechanical properties at 20 °C
| Rolling | Standard | Size, mm | Tension | Classifiers | $$\sigma _{U}$$, $$MPa$$ | d5, % | Treatment |
|---|---|---|---|---|---|---|---|
| Workpiece | OST 1-90126 - 85 | 830 | 3 |
Long-term strength
| Standard | Treatment | Температура испытаний, ° С | Постоянно приложенное напряжение, МПа | Время до разрушения в часах, ч |
|---|---|---|---|---|
| OST 1-90126 - 85 | Without heat treatment | 975 | 240 | 40 |
Standards
| Standard | Description |
|---|---|
| OST 1-90126 - 85 |
Description of chemical elements
| Element | Units of measurement | Description |
|---|---|---|
| Fe | % | Iron |
| Si | % | Silicon |
| B | % | Bor |
| Ca | % | Calcium |
| Mn | % | Manganese |
| Co | % | Cobalt |
| Cr | % | Chrome |
| Ti | % | Titan |
| Ni | % | Nickel |
| Zr | % | Zirconium |
| Al | % | Aluminium |
| Ce | % | Cerium |
| P | % | Phosphorus |
| C | % | Carbon |
| S | % | Sulfur |
| Nb | % | Niobium |
| La | % | Lanthanum |
| Y | % | Yttrium |
| Mo | % | Molybdenum |
| W | % | Tungsten |
| Hf | % | Hafnium |
Description of mechanical properties
| Parameter | Units of measurement | Description |
|---|---|---|
| d5 | % | Elongation at break |
| $$\sigma _{U}$$ | $$MPa$$ | Ultimate tensile strength |