ZhS6K (ZHS6K-VI)
Production of cast bar stock and ingots for remelting later in the casting of blades and other shaped castings
Classification
| Country | Section | Category |
|---|---|---|
| CIS, Russia, Ukraine | Heat resistant steels and alloys | Heat resistant alloys |
Chemical composition
| Standard | Fe, % | Si, % | B, % | Bi, % | Mn, % | Co, % | Cr, % | Ti, % | Ni, % | Zr, % | Al, % | Pb, % | Ce, % | P, % | C, % | S, % | Mo, % | W, % |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| OST 1-90126 - 85 | < 2 | < 0.4 | < 0.02 | < 0.0005 | < 0.4 | 4–5.5 | 9.5–12 | 2.5–3.2 | 60.1835–70.87 | < 0.04 | 5–6 | < 0.001 | < 0.025 | < 0.015 | 0.13–0.2 | < 0.015 | 3.5–4.5 | 4.5–5.5 |
Information on suppliers
Long-term strength
| Standard | Treatment | Температура испытаний, ° С | Постоянно приложенное напряжение, МПа | Время до разрушения в часах, ч |
|---|---|---|---|---|
| OST 1-90126 - 85 | Heating up to 1210 + 15 ° С, holding 4 hours, air cooling | 975 | 200 | 50 |
Note: According to OST 1 90127-85 under the same conditions. The time to destruction is at least 40 hours.
Standards
| Standard | Description |
|---|---|
| OST 1-90126 - 85 |
Description of chemical elements
| Element | Units of measurement | Description |
|---|---|---|
| Fe | % | Iron |
| Si | % | Silicon |
| B | % | Bor |
| Bi | % | Bismuth |
| Mn | % | Manganese |
| Co | % | Cobalt |
| Cr | % | Chrome |
| Ti | % | Titan |
| Ni | % | Nickel |
| Zr | % | Zirconium |
| Al | % | Aluminium |
| Pb | % | Lead |
| Ce | % | Cerium |
| P | % | Phosphorus |
| C | % | Carbon |
| S | % | Sulfur |
| Mo | % | Molybdenum |
| W | % | Tungsten |