ρ
kgm3
σU
MPa
σP
MPa
ϵL

MA2-1pch

for the manufacture of semi-hot deformation method; for the production of complex configuration of forgings for welded structures with extreme operating temperatures up to +150 ° C — for a long time, up to +200 ° C — momentarily.

Classification

Country	Section	Category
Country	Section	Category
CIS, Russia, Ukraine	Magnesium	Wrought Magnesium Alloys

Chemical composition

Standard	Fe, %	Si, %	Be, %	Mg, %	Mn, %	Cu, %	Zn, %	Ni, %	Al, %
Standard	Fe, %	Si, %	Be, %	Mg, %	Mn, %	Cu, %	Zn, %	Ni, %	Al, %
GOST 14957-76	< 0.005	< 0.01	< 0.002	92.872–95.2	0.2–0.6	< 0.01	0.8–1.5	< 0.001	3.8–5

Information on suppliers

Wish to advertise here?

Physical characteristics

Temperature, °C	$\rho$ , $\frac{kg}{m^3}$
Temperature, °C	$\rho$ , $\frac{kg}{m^3}$
20	1790

Mechanical properties at 20 °C

Rolling	Standard	Size, mm	Tension	Classifiers	$\sigma _{U}$ , $MPa$	$\sigma_{P}$ , $MPa$	$\epsilon_L$ , %	Treatment
Rolling	Standard	Size, mm	Tension	Classifiers	$\sigma _{U}$ , $MPa$	$\sigma_{P}$ , $MPa$	$\epsilon_L$ , %	Treatment
Sheet				annealing	260	150–160	8–10
Trumpet					230		8
Round					245–255	145	5–8
Sheet					230–250	140	6–8

Standards

Standard	Description
Standard	Description
GOST 14957-76

Description of chemical elements

Element	Units of measurement	Description
Element	Units of measurement	Description
Fe	%	Iron
Si	%	Silicon
Be	%	Beryllium
Mg	%	Magnesium
Mn	%	Manganese
Cu	%	Copper
Zn	%	Zinc
Ni	%	Nickel
Al	%	Aluminium

Description of physical characteristics

Parameter	Units of measurement	Description
Parameter	Units of measurement	Description
$\rho$	$\frac{kg}{m^3}$	The density of the material

Description of mechanical properties

Parameter	Units of measurement	Description
Parameter	Units of measurement	Description
$\sigma _{U}$	$MPa$	Ultimate tensile strength
$\sigma_{P}$	$MPa$	Proportionality limit
$\epsilon_L$	%	Elongation at break (longitudinal)