POSSu5-1

For tinning and soldering of components operating at elevated temperatures for tin plating of tubular radiators. antimony alloy

Classification

Country	Section	Category
Country	Section	Category
CIS, Russia, Ukraine	Tin, lead, babity	Tin-lead solder

Chemical composition

Standard	Fe, %	Sn, %	Bi, %	Cu, %	Zn, %	Ni, %	Sb, %	Al, %	Pb, %	As, %	S, %
Standard	Fe, %	Sn, %	Bi, %	Cu, %	Zn, %	Ni, %	Sb, %	Al, %	Pb, %	As, %	S, %
GOST 21930-76	< 0.02	4–5	< 0.2	< 0.08	< 0.002	< 0.08	0.5–1	< 0.002	93.776–95.5	< 0.02	< 0.02

Information on suppliers

Wish to advertise here?

Physical characteristics

Temperature, °C	$\rho$ , $\frac{kg}{m^3}$	$R\cdot 10^{-6}$ , $\Omega\cdot m$
Temperature, °C	$\rho$ , $\frac{kg}{m^3}$	$R\cdot 10^{-6}$ , $\Omega\cdot m$
20	11200	0.2

Mechanical properties at 20 °C

Rolling	Standard	Size, mm	Tension	Classifiers	$\sigma _{U}$ , $MPa$	$\epsilon_L$ , %	$KCU\cdot 10^{3}$ , $\frac{J}{m^2}$	Treatment
Rolling	Standard	Size, mm	Tension	Classifiers	$\sigma _{U}$ , $MPa$	$\epsilon_L$ , %	$KCU\cdot 10^{3}$ , $\frac{J}{m^2}$	Treatment
Alloy	GOST 21930-76				33	40	280

Brinell hardness number

Rolling	Standard	Classifiers	Value, HBW
Rolling	Standard	Classifiers	Value, HBW
Alloy	GOST 21930-76		107

Casting and technological parameters

melting point, solidus, °C	melting point, liquidus, °C
melting point, solidus, °C	melting point, liquidus, °C
275	308

Standards

Standard	Description
Standard	Description
GOST 21930-76

Description of chemical elements

Element	Units of measurement	Description
Element	Units of measurement	Description
Fe	%	Iron
Sn	%	Tin
Bi	%	Bismuth
Cu	%	Copper
Zn	%	Zinc
Ni	%	Nickel
Sb	%	Antimony
Al	%	Aluminium
Pb	%	Lead
As	%	Arsenic
S	%	Sulfur

Description of physical characteristics

Parameter	Units of measurement	Description
Parameter	Units of measurement	Description
$\rho$	$\frac{kg}{m^3}$	The density of the material
$R\cdot 10^{-6}$	$\Omega\cdot m$	Electrical resistivity

Description of mechanical properties

Parameter	Units of measurement	Description
Parameter	Units of measurement	Description
$\sigma _{U}$	$MPa$	Ultimate tensile strength
$\epsilon_L$	%	Elongation at break (longitudinal)
$KCU\cdot 10^{3}$	$\frac{J}{m^2}$	Impact toughness

Description of the casting and technological parameters

Parameter	Units of measurement	Description
Parameter	Units of measurement	Description
melting point, solidus	°C	The temperature at which melts the low melting component
melting point, liquidus	°C	The temperature at which equilibrium falls first crystal