SHH15SG
Substitute: HVG, ShH15, 9HS, HVSG
Large ring ball and roller bearings with a wall thickness of 20−30 mm balls with a diameter more than 50 mm; rollers with a diameter of over 35 mm.
Substitute: HVG, ShH15, 9HS, HVSG
Large ring ball and roller bearings with a wall thickness of 20−30 mm balls with a diameter more than 50 mm; rollers with a diameter of over 35 mm.
Standard | Fe, % | Si, % | Mn, % | Cr, % | Ti, % | Cu, % | Ni, % | P, % | C, % | S, % | O, % |
---|---|---|---|---|---|---|---|---|---|---|---|
Standard | Fe, % | Si, % | Mn, % | Cr, % | Ti, % | Cu, % | Ni, % | P, % | C, % | S, % | O, % |
GOST 801-78 | > 94.8415 | 0.4–0.65 | 0.9–1.2 | 1.3–1.65 | < 0.01 | < 0.25 | < 0.3 | < 0.027 | 0.95–1.05 | < 0.02 | < 0.0015 |
Rolling | Standard | Size, mm | Tension | Classifiers | \sigma _{U} |
\sigma_{P} |
\psi |
KCU\cdot 10^{3} |
d5, % | Treatment |
---|---|---|---|---|---|---|---|---|---|---|
Rolling | Standard | Size, mm | Tension | Classifiers | \sigma _{U}, MPa | \sigma_{P}, MPa | \psi, % | KCU\cdot 10^{3}, \frac{J}{m^2} | d5, % | Treatment |
Steel | GOST 801-78 | annealing | 590–730 | 370–410 | 45 | 440 | 20 | Annealing 790-810 ° C, furnace cooled, 15 ° C / h |
Rolling | Standard | Classifiers | Value, HBW |
---|---|---|---|
Rolling | Standard | Classifiers | Value, HBW |
Rental hot rolled. | GOST 801-78 | hot rolling | 179–217 |
USA | Germany |
---|---|
USA | Germany |
K19195 | 1.3520 (100CrMn6) |
Standard | Description |
---|---|
Standard | Description |
GOST 801-78 |
Parameter | Units of measurement | Description |
---|---|---|
Parameter | Units of measurement | Description |
d5 | % | Elongation at break |
\sigma _{U} |
MPa |
Ultimate tensile strength |
\sigma_{P} |
MPa |
Proportionality limit |
\psi |
% | Reduction in cross section on fracture |
KCU\cdot 10^{3} |
\frac{J}{m^2} |
Impact toughness |