Precision alloy 30NGHTYUM

No foreign analogues

Used for the manufacture of cores of magnetic amplifiers, switching chokes, rectifier units

Classification

Country	Section	Category
CIS, Russia, Ukraine	Precision alloys	Soft Magnetic Precision Alloys

Chemical composition

Standard	Fe, %	Si, %	Mn, %	Cr, %	Ti, %	Ni, %	Al, %	Mo, %	ET, %
GOST 10994-74	39.93–45.9	< 0.5	5–6	12–13	2.7–3.2	29–31	0.9–1.3	4.5–5	< 0.07

Information on suppliers

Wish to advertise here?

Physical characteristics

Temperature, °C	$$\alpha\cdot 10^{6}$$, $$K^{-1}$$	$$\varkappa$$, $$\frac{W}{m\cdot K}$$	$$\rho$$, $$\frac{kg}{m^3}$$	Cp, Дж/кг·К
20	16.2	64.4	8350	456

Mechanical properties at 20 °C

Rolling	Standard	Size, mm	Tension	Classifiers	$$\sigma _{U}$$, $$MPa$$	$$\sigma_{Y}$$, $$MPa$$	d5, %	Treatment
Tape	TU 14-1-1168-75	<2.0	Transverse		500	145	20

Brinell hardness number

Rolling	Standard	Classifiers	Value, HBW
Tape	TU 14-1-1168-75		120–150

Technological Properties

Weldability	Flake Susceptibility	Propensity to temper brittleness
Difficult to weld	insensitive	loathsome

Standards

Standard	Description
GOST 10994-74

Description of chemical elements

Element	Units of measurement	Description
ET	%	Total other items
Fe	%	Iron
Si	%	Silicon
Mn	%	Manganese
Cr	%	Chrome
Ti	%	Titan
Ni	%	Nickel
Al	%	Aluminium
Mo	%	Molybdenum

Description of physical characteristics

Parameter	Units of measurement	Description
Cp	Дж/кг·К	Specific heat of material
$$\alpha\cdot 10^{6}$$	$$K^{-1}$$	Coefficient of thermal (linear) expansion (range 20°C–T)
$$\varkappa$$	$$\frac{W}{m\cdot K}$$	Coefficient of thermal conductivity (the heat capacity of the material)
$$\rho$$	$$\frac{kg}{m^3}$$	The density of the material

Description of mechanical properties

Parameter	Units of measurement	Description
d5	%	Elongation at break
$$\sigma_{Y}$$	$$MPa$$	Yield strength
$$\sigma _{U}$$	$$MPa$$	Ultimate tensile strength

Designation of types of weldability

Parameter	Units of measurement	Description
no limits		Welding is performed without heating and without subsequent heat treatment
Boundedly welded		Welding is possible with heating up to 100–120 °C and subsequent heat treatment
Difficult to weld		For obtaining quality welded joints, additional operations are required: heating up to 200–300 °C for welding, heat treatment after welding — annealing
Not applicable for welded structures