Precision alloy 31NH3G

No foreign analogues

It is used for structures and pipelines operating at low temperatures; TKLR * 1,000,000 in the temperature range from -258 to +20 and from +20 to +100 ºC no more than 1.0−2.0 [1 / ºC]

Classification

Country Section Category
CIS, Russia, Ukraine Precision alloys With given TCLE

Chemical composition

Standard Fe, % Si, % Mn, % Cr, % Ni, % ET, %
GOST 10994-74 62.81–65.1 0.3–0.6 0.3–0.7 3.3–3.8 31–32 < 0.09

Information on suppliers

Physical characteristics

Temperature, °C $$E\cdot 10^{9}$$, $$MPa$$ $$\rho$$, $$\frac{kg}{m^3}$$ $$R\cdot 10^{-6}$$, $$\Omega\cdot m$$
20 143 8200 760

Mechanical properties at 20 °C

Rolling Standard Size, mm Tension Classifiers $$\sigma _{U}$$, $$MPa$$ $$\sigma_{Y}$$, $$MPa$$ d5, % Treatment
Tape GOST 10994-74 50 Transverse 190–210 25–35

Mechanical properties at 25 °C

Rolling Standard Size, mm Tension Classifiers $$\sigma _{U}$$, $$MPa$$ $$\sigma_{Y}$$, $$MPa$$ d5, % Treatment
50 400–450

Brinell hardness number

Rolling Standard Classifiers Value, HBW
Tape GOST 10994-74 120–150

Casting and technological parameters

melting point, °C
1450

Limit operating modes

Standard Температура, °C
GOST 10994-74 < 150

Heat Treatment Modes

Treatment
Отжиг

Analogues

Russia
Сплав ЭП545

Standards

Standard Description
GOST 10994-74

Description of chemical elements

Element Units of measurement Description
ET % Total other items
Fe % Iron
Si % Silicon
Mn % Manganese
Cr % Chrome
Ni % Nickel

Description of physical characteristics

Parameter Units of measurement Description
$$E\cdot 10^{9}$$ $$MPa$$ Elastic modulus
$$\rho$$ $$\frac{kg}{m^3}$$ The density of the material
$$R\cdot 10^{-6}$$ $$\Omega\cdot m$$ Electrical resistivity

Description of mechanical properties

Parameter Units of measurement Description
d5 % Elongation at break
$$\sigma_{Y}$$ $$MPa$$ Yield strength
$$\sigma _{U}$$ $$MPa$$ Ultimate tensile strength

Description of the casting and technological parameters

Parameter Units of measurement Description
melting point °C The temperature at which solid crystalline body makes the transition to the liquid state and Vice versa