St4kp (VSt4kp)
I-beam, channel, angle steel
Classification
| Country |
Section |
Category |
| CIS, Russia, Ukraine |
Structural steel |
Carbonaceous structural steel of ordinary quality |
Chemical composition
| Standard |
Fe, % |
Si, % |
Mn, % |
Cr, % |
Cu, % |
Ni, % |
As, % |
P, % |
C, % |
S, % |
N, % |
|---|
| GOST 380-2005 |
97.902–99.42 |
< 0.05 |
0.4–0.7 |
< 0.3 |
< 0.3 |
< 0.3 |
< 0.08 |
< 0.04 |
0.18–0.27 |
< 0.05 |
< 0.008 |
Information on suppliers
Physical characteristics
| Temperature, °C |
$$\rho$$, $$\frac{kg}{m^3}$$ |
|---|
| 20 |
7850 |
Mechanical properties at 20 °C
| Rolling |
Standard |
Size, mm |
Tension |
Classifiers |
$$\sigma _{U}$$, $$MPa$$ |
$$\sigma_{P}$$, $$MPa$$ |
$$\epsilon_L$$, % |
Treatment |
|---|
| Trumpet |
GOST 10705-80 |
|
|
|
412 |
245 |
21 |
|
| Hire |
GOST 535-2005 |
|
|
|
400–510 |
225–255 |
22–25 |
|
Brinell hardness number
| Rolling |
Standard |
Classifiers |
Value, HBW |
| Alloy |
|
|
1430 |
Technological Properties
| Weldability |
|---|
| Boundedly welded |
Analogues
Standards
Description of chemical elements
| Element |
Units of measurement |
Description |
| Fe |
% |
Iron |
| Si |
% |
Silicon |
| Mn |
% |
Manganese |
| Cr |
% |
Chrome |
| Cu |
% |
Copper |
| Ni |
% |
Nickel |
| As |
% |
Arsenic |
| P |
% |
Phosphorus |
| C |
% |
Carbon |
| S |
% |
Sulfur |
| N |
% |
Nitrogen |
Description of physical characteristics
| Parameter |
Units of measurement |
Description |
| $$\rho$$ |
$$\frac{kg}{m^3}$$ |
The density of the material |
Description of mechanical properties
| Parameter |
Units of measurement |
Description |
| $$\sigma _{U}$$ |
$$MPa$$ |
Ultimate tensile strength |
| $$\sigma_{P}$$ |
$$MPa$$ |
Proportionality limit |
| $$\epsilon_L$$ |
% |
Elongation at break (longitudinal) |
Designation of types of weldability
| Parameter |
Units of measurement |
Description |
| no limits |
|
Welding is performed without heating and without subsequent heat treatment |
| Boundedly welded |
|
Welding is possible with heating up to 100–120 °C and subsequent heat treatment |
| Difficult to weld |
|
For obtaining quality welded joints, additional operations are required: heating up to 200–300 °C for welding, heat treatment after welding — annealing |
| Not applicable for welded structures |
|
|