Steel corrosion resistant heat resisting 30X23H7C

No foreign analogues

Used for the manufacture of pipelines and high-temperature equipment for oil refining and petrochemical industries

Classification

Country Section Category
CIS, Russia, Ukraine Heat resistant steels and alloys Heat resistant high alloy steel

Chemical composition

Standard Fe, % Si, % Mn, % Cr, % Ti, % Cu, % Ni, % V, % C, % Mo, % ET, %
GOST 5949-18 63.44–71.799 0.5–1.2 0.5–0.85 21–25 0.0005–0.1 < 0.3 6–8 0.0005–0.2 0.2–0.3 < 0.5 < 0.11

Information on suppliers

Physical characteristics

Temperature, °C $$E\cdot 10^{9}$$, $$MPa$$ $$\alpha\cdot 10^{6}$$, $$K^{-1}$$ $$\varkappa$$, $$\frac{W}{m\cdot K}$$ $$\rho$$, $$\frac{kg}{m^3}$$
20 198 13.2 14 7800

Mechanical properties at 20 °C

Rolling Standard Size, mm Tension Classifiers $$\sigma _{U}$$, $$MPa$$ $$\sigma_{Y}$$, $$MPa$$ d5, % Treatment
Round GOST 5949-18 50 Transverse 580–620 280–330 25–30

Твёрдость по Роквеллу

Rolling Standard Classifiers Value, HRC
Round GOST 5949-18 30–32

Technological Properties

Weldability Flake Susceptibility Propensity to temper brittleness
no limits not sensitive loathsome

Limit operating modes

Standard Температура, °C
GOST 5949-18 < 850

Wärmebehandlungsmodi

Verarbeitung
Härten

Standards

Standard Description
GOST 5949-18
TU 1333-047-00220302-02

Description of chemical elements

Element Units of measurement Description
ET % Total other items
Fe % Iron
Si % Silicon
Mn % Manganese
Cr % Chrome
Ti % Titan
Cu % Copper
Ni % Nickel
V % Vanadium
C % Carbon
Mo % Molybdenum

Description of physical characteristics

Parameter Units of measurement Description
$$E\cdot 10^{9}$$ $$MPa$$ Elastic modulus
$$\alpha\cdot 10^{6}$$ $$K^{-1}$$ Coefficient of thermal (linear) expansion (range 20°C–T)
$$\varkappa$$ $$\frac{W}{m\cdot K}$$ Coefficient of thermal conductivity (the heat capacity of the material)
$$\rho$$ $$\frac{kg}{m^3}$$ The density of the material

Description of mechanical properties

Parameter Units of measurement Description
d5 % Elongation at break
$$\sigma_{Y}$$ $$MPa$$ Yield strength
$$\sigma _{U}$$ $$MPa$$ Ultimate tensile strength

Designation of types of weldability

Parameter Units of measurement Description
no limits Welding is performed without heating and without subsequent heat treatment
Boundedly welded Welding is possible with heating up to 100–120 °C and subsequent heat treatment
Difficult to weld For obtaining quality welded joints, additional operations are required: heating up to 200–300 °C for welding, heat treatment after welding — annealing
Not applicable for welded structures