EP602-VI (X28-VI)

Classification

Country Section Category
CIS, Russia, Ukraine Heat resistant steels and alloys Heat resistant alloys

Chemical composition

Standard Fe, % Si, % Mn, % Cr, % Ni, % P, % C, % S, %
TU 14-1-1019-74 68.402–73 < 0.25 < 0.8 27–30 < 0.5 < 0.02 < 0.008 < 0.02

Information on suppliers

Physical characteristics

Temperature, °C $$E\cdot 10^{9}$$, $$MPa$$ $$\alpha\cdot 10^{6}$$, $$K^{-1}$$ $$\rho$$, $$\frac{kg}{m^3}$$
20 200 9.5 7600

Mechanical properties at 20 °C

Rolling Standard Size, mm Tension Classifiers $$\sigma _{U}$$, $$MPa$$ $$\sigma_{Y}$$, $$MPa$$ d5, % Treatment
Trumpet TU 14-1-1019-74 400 Transverse > 440 295 17

Brinell hardness number

Rolling Standard Classifiers Value, HBW
Trumpet TU 14-1-1019-74 240–260

Technological Properties

Weldability Flake Susceptibility Propensity to temper brittleness
Boundedly welded insensitive inclined

Limit operating modes

Standard Температура, °C
TU 14-1-1019-74 < 200

Properties

Property
Ferritic grade steel

Standards

Standard Description
TU 14-1-1019-74

Description of chemical elements

Element Units of measurement Description
Fe % Iron
Si % Silicon
Mn % Manganese
Cr % Chrome
Ni % Nickel
P % Phosphorus
C % Carbon
S % Sulfur

Description of physical characteristics

Parameter Units of measurement Description
$$E\cdot 10^{9}$$ $$MPa$$ Elastic modulus
$$\alpha\cdot 10^{6}$$ $$K^{-1}$$ Coefficient of thermal (linear) expansion (range 20°C–T)
$$\rho$$ $$\frac{kg}{m^3}$$ The density of the material

Description of mechanical properties

Parameter Units of measurement Description
d5 % Elongation at break
$$\sigma_{Y}$$ $$MPa$$ Yield strength
$$\sigma _{U}$$ $$MPa$$ Ultimate tensile strength

Designation of types of weldability

Parameter Units of measurement Description
no limits Welding is performed without heating and without subsequent heat treatment
Boundedly welded Welding is possible with heating up to 100–120 °C and subsequent heat treatment
Difficult to weld For obtaining quality welded joints, additional operations are required: heating up to 200–300 °C for welding, heat treatment after welding — annealing
Not applicable for welded structures