St-06H19N9T (H-60)
Welding wire cold drawn alloy steel welding (surfacing), and the manufacture of electrodes
Welding wire cold drawn alloy steel welding (surfacing), and the manufacture of electrodes
| Standard | Fe, % | Si, % | Mn, % | Cr, % | Ti, % | Ni, % | P, % | C, % | S, % |
|---|---|---|---|---|---|---|---|---|---|
| Standard | Fe, % | Si, % | Mn, % | Cr, % | Ti, % | Ni, % | P, % | C, % | S, % |
| GOST 2246-70 | 65.875–72.1 | 0.4–1 | 1–2 | 18–20 | 0.5–1 | 8–10 | < 0.03 | < 0.08 | < 0.015 |
| Property |
|---|
| Property |
| Note Fluctuations in the tensile strength in one coil of wire with a diameter of more than 1.4 mm should not exceed 90 N / mm2. |
| For welding Diameter: 0.3 - 0.5 mm; Temporary resistance: 890 - 1390 MP |
| Diameter: 0.8 - 1.5 mm; Temporary resistance: 890 - 1340 MPa |
| Diameter: 0.8 - 1.5 mm; Temporary resistance: 890 - 1340 MPa |
| Diameter: 1.6mm; Temporary resistance: 890 - 1290 MPa |
| Diameter: 2mm; Temporary resistance: 790 - 1190 MPa |
| Diameter:> 2 mm; Temporary resistance: 690 - 1040 MPa |
| For the manufacture of electrodes Diameter: 1.6 mm; Temporary resistance: 690 - 990 MPa |
| Diameter: 2mm; Temporary resistance: 690 - 990 MPa |
| Diameter:> 2 mm; Temporary resistance: 640 - 940 MPa |
| Density: 7.77 g / cm3 |
| Standard | Description |
|---|---|
| Standard | Description |
| GOST 2246-70 | |
| OST 26-291-94 |