St-08GA
Welding cold drawn wire of low carbon steel welding (surfacing), and the manufacture of electrodes
Welding cold drawn wire of low carbon steel welding (surfacing), and the manufacture of electrodes
| Standard | Fe, % | Si, % | Mn, % | Cr, % | Ni, % | P, % | C, % | S, % | N, % |
|---|---|---|---|---|---|---|---|---|---|
| Standard | Fe, % | Si, % | Mn, % | Cr, % | Ni, % | P, % | C, % | S, % | N, % |
| GOST 2246-70 | 98.325–99.2 | < 0.06 | 0.8–1.1 | < 0.1 | < 0.25 | < 0.03 | < 0.1 | < 0.025 | < 0.01 |
| Property |
|---|
| Property |
| Wire according to TU 14-1-953-74 Diameter: 2 mm; Temporary resistance: 784 - 1176 MPa |
| Diameter: 2.5 - 3.0 mm; Temporary resistance: 686 - 1029 MPa |
| Wire according to TU 14-4-863-77 Thickness: 0.8 - 1.4 mm; Temporary resistance: 880 - 1250 MPa |
| Thickness: 1.6 mm; Temporary resistance: 880 - 1180 MPa |
| Thickness: 2 mm; Temporary resistance: 780 - 1080 MPa |
| Density: 7.86 g / cm3 |
| Standard | Description |
|---|---|
| Standard | Description |
| GOST 2246-70 | |
| TU 1227-001-10531968-2003 | |
| TU 1211-037-00187240-2006 | |
| TU 14-1-953-74 | |
| TU 14-15-346-94 | |
| TU 14-15-345-94 | |
| TU 14-15-373-95 | |
| TU 14-4-1877-2004 | |
| TU 14-4-863-77 | |
| TU У 27.1-4-548-2003 |