Sv-08GS

Welding cold drawn wire of stainless steel, for welding (welding) and the manufacture of electrodes

Classification

Country	Section	Category
CIS, Russia, Ukraine	Materials for welding and soldering	Steel welding wire

Chemical composition

Standard	Fe, %	Si, %	Mn, %	Cr, %	Ni, %	P, %	C, %	S, %	N, %
GOST 2246-70	96.835–98	0.6–0.85	1.4–1.7	< 0.2	< 0.25	< 0.03	< 0.1	< 0.025	< 0.01

Information on suppliers

Wish to advertise here?

Properties

Property
Note Fluctuations in the tensile strength in one coil of wire with a diameter of more than 1.4 mm should not exceed 90 N / mm2.
For welding Diameter: 0.3 - 0.5 mm; Temporary resistance: 890 - 1390 MPa
Diameter: 0.8 - 1.5 mm; Temporary resistance: 890 - 1340 MPa
Diameter: 1.6mm; Temporary resistance: 890 - 1290 MPa
Diameter: 2mm; Temporary resistance: 790 - 1190 MPa
Diameter:> 2 mm; Temporary resistance: 690 - 1040 MPa
For the manufacture of electrodes Diameter: 1.6 mm; Temporary resistance: 690 - 990 MPa
Diameter: 2mm; Temporary resistance: 690 - 990 MPa
Diameter:> 2 mm; Temporary resistance: 640 - 940 MPa
Wire according to TU 14-1-953-74 Diameter: 2 mm; Temporary resistance: 784 - 1176 MPa
Diameter: 2.5 - 3.0 mm; Temporary resistance: 686 - 1029 MPa
Wire according to TU 14-4-863-77 Thickness: 0.8 - 1.4 mm; Temporary resistance: 880 - 1250 MPa
Thickness: 1.6 mm; Temporary resistance: 880 - 1180 MPa
Thickness: 2 mm; Temporary resistance: 780 - 1080 MPa
Density: 7.82 g / cm3

Analogues

Germany
1.5125

Standards

Standard	Description
GOST 2246-70
TU 14-1-953-74
TU 14-4-863-77
TU У 14-4-495-2001

Description of chemical elements

Element	Units of measurement	Description
Fe	%	Iron
Si	%	Silicon
Mn	%	Manganese
Cr	%	Chrome
Ni	%	Nickel
P	%	Phosphorus
C	%	Carbon
S	%	Sulfur
N	%	Nitrogen