St-08HMNFBA (H-49)
Welding cold drawn wire of stainless steel, for welding (welding) and the manufacture of electrodes
Classification
Country | Section | Category |
---|---|---|
CIS, Russia, Ukraine | Materials for welding and soldering | Steel welding wire |
Chemical composition
Standard | Fe, % | Si, % | Mn, % | Cr, % | Ni, % | V, % | P, % | C, % | S, % | Nb, % | Mo, % | N, % |
---|---|---|---|---|---|---|---|---|---|---|---|---|
GOST 2246-70 | 95.055–96.62 | 0.12–0.3 | 0.35–0.6 | 1.1–1.4 | 0.65–0.9 | 0.2–0.35 | < 0.025 | 0.06–0.1 | < 0.025 | 0.1–0.23 | 0.8–1 | < 0.015 |
Information on suppliers
Properties
Property |
---|
Note Fluctuations in the tensile strength in one coil of wire with a diameter of more than 1.4 mm should not exceed 90 N / mm2. |
For welding Diameter: 0.3 - 0.5 mm; Temporary resistance: 890 - 1390 MPa |
Diameter: 0.8 - 1.5 mm; Temporary resistance: 890 - 1340 MPa |
Diameter: 1.6mm; Temporary resistance: 890 - 1290 MPa |
Diameter: 2mm; Temporary resistance: 790 - 1190 MPa |
Diameter:> 2 mm; Temporary resistance: 690 - 1040 MPa |
For the manufacture of electrodes Diameter: 1.6 mm; Temporary resistance: 690 - 990 MPa |
Diameter: 2mm; Temporary resistance: 690 - 990 MP |
Diameter:> 2 mm; Temporary resistance: 640 - 940 MPa |
Density: 7.87 g / cm3 |
Standards
Standard | Description |
---|---|
GOST 2246-70 |
Description of chemical elements
Element | Units of measurement | Description |
---|---|---|
Fe | % | Iron |
Si | % | Silicon |
Mn | % | Manganese |
Cr | % | Chrome |
Ni | % | Nickel |
V | % | Vanadium |
P | % | Phosphorus |
C | % | Carbon |
S | % | Sulfur |
Nb | % | Niobium |
Mo | % | Molybdenum |
N | % | Nitrogen |