Sv-09HGNMTA
Classification
Chemical composition
| Standard | Fe, % | Si, % | Sn, % | Mn, % | Co, % | Cr, % | Ti, % | Cu, % | Ni, % | Sb, % | V, % | Al, % | As, % | P, % | C, % | S, % | Mo, % | N, % |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Standard | Fe, % | Si, % | Sn, % | Mn, % | Co, % | Cr, % | Ti, % | Cu, % | Ni, % | Sb, % | V, % | Al, % | As, % | P, % | C, % | S, % | Mo, % | N, % |
| TU 14-1-3675-2001 | 93.807–95.81 | 0.17–0.3 | < 0.001 | 0.8–1.5 | < 0.03 | 1.6–1.9 | 0.05–0.11 | < 0.1 | 1–1.3 | < 0.008 | < 0.03 | < 0.05 | < 0.01 | < 0.012 | 0.07–0.11 | < 0.012 | 0.5–0.7 | < 0.02 |
Information on suppliers
Properties
| Property |
|---|
| Property |
| Note Fluctuations in the tensile strength in one coil of wire with a diameter of more than 1.4 mm should not exceed 90 N / mm2. |
| For welding Diameter: 0.3 - 0.5 mm; Temporary resistance: 890 - 1390 MPa |
| Diameter: 0.8 - 1.5 mm; Temporary resistance: 890 - 1340 MPa |
| Diameter: 1.6mm; Temporary resistance: 890 - 1290 MPa |
| Diameter: 2mm; Temporary resistance: 790 - 1190 MPa |
| Diameter:> 2 mm; Temporary resistance: 690 - 1040 MPa |
| For the manufacture of electrodes Diameter: 1.6 mm; Temporary resistance: 690 - 990 MPa |
| Diameter: 2mm; Temporary resistance: 690 - 990 MPa |
| Diameter:> 2 mm; Temporary resistance: 640 - 940 MPa |
| Density: 7.86 g / cm3 |
Standards
| Standard | Description |
|---|---|
| Standard | Description |
| TU 14-1-3675-2001 |
Description of chemical elements
| Element | Units of measurement | Description |
|---|---|---|
| Element | Units of measurement | Description |
| Fe | % | Iron |
| Si | % | Silicon |
| Sn | % | Tin |
| Mn | % | Manganese |
| Co | % | Cobalt |
| Cr | % | Chrome |
| Ti | % | Titan |
| Cu | % | Copper |
| Ni | % | Nickel |
| Sb | % | Antimony |
| V | % | Vanadium |
| Al | % | Aluminium |
| As | % | Arsenic |
| P | % | Phosphorus |
| C | % | Carbon |
| S | % | Sulfur |
| Mo | % | Molybdenum |
| N | % | Nitrogen |